Polymers and compounds based on dipyrrolo[1,2-B:1&#39;,2&#39;-G][2,6]naphthyridine-5,11-dione

ABSTRACT

Polymers containing a repeating unit of the formula —[Ar—Y—Ar′]— (V), and compounds of formula R 10 —Ar—Y—Ar′—R 10′  (I), where Y is a group of formula 
                         
and organic devices containing the polymers. The polymers and compounds have excellent solubility in organic solvents and excellent film-forming properties. In addition, high efficiency of energy conversion, excellent field-effect mobility, good on/off current ratios and/or excellent stability can be observed, when the polymers and compounds are used in organic field effect transistors, organic photovoltaics and photodiodes.

The present invention relates to polymers comprising a repeating unit of the formula (V), and compounds of formula (I) and their use as organic semiconductor in organic devices, especially in organic photovoltaics and photodiodes, or in a device containing a diode and/or an organic field effect transistor. The polymers and compounds according to the invention can have excellent solubility in organic solvents and excellent film-forming properties. In addition, high efficiency of energy conversion, excellent field-effect mobility, good on/off current ratios and/or excellent stability can be observed, when the polymers and compounds according to the invention are used in organic field effect transistors, organic photovoltaics and photodiodes.

Daniel D. Gryko et al., Chem. Commun., 2016, 52, 5108 [publication date: Mar. 31, 2016] reports the synthesis of red-emissive dyes based on dipyrrolo[1,2-b:10,20-g][2,6]naphthyridine-5,11-dione (DPND) having intense fluorescence in the range of 520-740 nm.

Photophysical properties of DPND dyes measured in dichloromethane are shown in Tab. 2:

λ^(max) _(abs) ε_(max) λ^(max) _(em) δ_(v) ^(a) Dye [nm] [M⁻¹ cm⁻¹] [nm] θ_(fl) [cm⁻¹] 1a 509 26600 535 0.61^(b) 950 1b 499 29200 523 0.66^(b) 900 1c 504 29300 528 0.71^(b) 900 1d 505 23100 543 0.58^(b) 1400 1e 510 28300 536 0.26^(b) 950 1f 500 28000 526 0.67^(b) 1000 4 503 24600 601 0.46^(b) 3240 5 520 34200 549 0.21^(b) 1000 6 517 34600 537 0.25^(b) 720 7a 599 57300 633 0.51^(c) 900 7b 584 47400 616 0.51^(c) 900 7c 601 52400 643 0.59^(c) 1100 7d 645 56600 736 0.17^(c) 1900 ^(a)Stokes shift i.e. the difference between the lowest energy absorption band and the highest energy emission band expressed in cm⁻¹. ^(b)Reference: rhodamine 6G in EtOH (θ_(fl) = 0.94). ^(c)Reference: cresyl violet in MeOH (θ_(fl) = 0.54).  

  1a, R = H 1b, R = CH₃ 1c, R = C₇H₁₅ 1d, R = sec-Butyl 1e, R = 4-Methoxybenzyl 1f, R = C₂H₅,  

  4, Y = COCF₃ 5, Y = Br 6, Y = CN,  

  7a, X = NO₂ 7b, X = CF₃ 7c, X = OCH₃ 7d, X = N(CH₃)₂.

All compounds 1a-f show intense structured absorption bands with the maxima at around 500 nm and the molecular absorption coefficients ranging from 24 000 to 29 000 M⁻¹ cm⁻¹. Except for 1e, all of the samples show good fluorescence quantum yields (0.58-0.71) and small Stokes shifts (˜1000 cm⁻¹). The presence of phenylethynyl substituents in dyes 7a-d caused a large bathochromic shift of the absorption by 80-140 nm in comparison with the starting DPND 1c.

WO08107089 relates to silylethynylated heteroacenes and formulations and electronic devices made with those compounds.

WO13050401 relates to polymers comprising one or more (repeating) unit(s) of the formula

and compounds of formula

wherein Y, Y¹⁵, Y¹⁶ and Y¹⁷ are independently of each other a group of formula

and their use as IR absorber, organic semiconductor in organic devices, especially in organic photovoltaics and photodiodes, or in a device containing a diode and/or an organic field effect transistor.

WO14072292 relates to polymers comprising one or more (repeating) unit(s) of the formula

and compounds of formula

wherein Y, Y¹⁵, Y¹⁶ and Y¹⁷ are independently of each other a group of formula

and their use as IR absorber, organic semiconductor in organic devices, especially in organic photovoltaics and photodiodes, or in a device containing a diode and/or an organic field effect transistor.

The present invention relates to compounds of formula R¹⁰—Ar—Y—Ar′—R^(10′)  (I), wherein

Ar is a group of formula —[Ar³]_(c)—[Ar²]_(b)—[Ar¹]_(a)—**,

Ar′ is a group of formula **—[Ar^(1′) ]_(a′)—[Ar²′]_(b′)—[Ar³′]_(c′)—,

Y is a group of formula

** indicates the bonding to Y,

a is 0, 1, 2, or 3, a′ is 0, 1, 2, or 3; b is 0, 1, 2, or 3; b′ is 0, 1, 2, or 3; c is 0, 1, 2, or 3; c′ is 0, 1, 2, or 3; m1 is 0, 1, or 2, m2 is 0, 1, or 2,

U¹ is O, or S,

U² is O, or S,

T¹, T², T³ and T⁴ are independently of each other hydrogen, halogen, cyano, —COOR¹⁰³, —OCOR¹⁰³, —NR¹¹²COR¹⁰³, —CONR¹¹²R¹¹³, —OR^(103′), —SR^(103′), —SOR^(103′), —SO₂R^(103′), —NR¹¹²SO₂R^(103′), —NR¹¹²R¹¹³, —NO₂, C₇-C₂₅arylalkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy;

a C₁-C₁₀₀alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—,

a C₂-C₁₀₀alkenyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—,

a C₂-C₁₀₀alkinyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—,

a C₃-C₁₂cycloalkyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—,

a C₆-C₂₄aryl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si);

a C₂-C₂₀heteroaryl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si);

a —CO—C₁-C₁₈alkyl group, a —CO—C₅-C₁₂cycloalkyl group, or —COO—C₁-C₁₈alkyl group;

Ar¹ and Ar^(1′) are independently of each other

Ar², Ar²′, Ar³ and Ar³′ have independently of each other the meaning of Ar¹, or are independently of each other

X is O, S, Se, Te, or NR⁸,

X′ is O, or S,

X¹, X² and X³ are independently of each other S, O, NR¹⁰⁷, —Si(R¹¹⁷)(R^(117′))—, —Ge(R¹¹⁷)(R^(117′))—, —C(R¹⁰⁸)(R¹⁰⁹)—, —C(═O)—, —C(═CR¹¹⁰R¹¹¹)—,

X⁴ and X^(4′) are independently of each other S, O, NR¹⁰⁷—, —Si(R¹¹⁷)(R^(117′))—, —Ge(R¹¹⁷)(R^(117′))—, —C(R¹⁰⁸)(R¹⁰⁹)—, —C(═O)—, —C(═CR¹¹⁰R¹¹¹)—,

R³ and R^(3′) are independently of each other hydrogen, halogen, halogenated C₁-C₂₅alkyl, especially CF₃, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₇-C₂₅arylalkyl, or C₁-C₂₅alkoxy;

R⁴, R^(4′), R⁵, R^(5′), R⁶, and R^(6′) are independently of each other hydrogen, halogen, halogenated C₁-C₂₅alkyl, especially CF₃, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₇-C₂₅arylalkyl, or C₁-C₂₅alkoxy;

R⁷, R^(7′), R⁹ and R^(9′) are independently of each other hydrogen, C₁-C₂₅alkyl, which may optionally be interrupted by one, or more oxygen, or sulphur atoms; or C₇-C₂₅arylalkyl,

R⁸ and R^(8′) are independently of each other hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; or C₇-C₂₅arylalkyl,

R¹⁰ and R^(10′) are independently of each other hydrogen, halogen, NO₂, NR¹¹²R¹¹³, cyano, C₁-C₂₅alkyl, C₁-C₂₅alkyl which is substituted one or more times by E (CF₃) and/or interrupted one or more times by D,

COO—C₁-C₁₈alkyl, C₄-C₁₈cycloalkyl group, C₄-C₁₈cycloalkyl group, which is substituted by G, C₂-C₁₈alkenyl, C₂-C₁₈alkynyl, C₁-C₁₈alkylthio, C₁-C₁₈alkoxy, C₁-C₁₈alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by G, or a group of formulae IVa to IVk,

X⁵ is O, S, Se, Te, or NR⁵⁹,

R¹¹ and R^(11′) are independently of each other C₁-C₂₅alkyl group, C₇-C₂₅arylalkyl, or a phenyl group, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy;

R¹² and R^(12′) are independently of each other hydrogen, halogen, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one, or more oxygen, or sulphur atoms, C₁-C₂₅alkoxy, C₇-C₂₅arylalkyl, or

R¹³ is a C₁-C₁₀alkyl group, or a tri(C₁-C₈alkyl)silyl group;

R²² to R²⁶ and R²⁹ to R⁵⁸ represent independently of each other H, halogen, cyano, NO₂, NR¹¹²R¹¹³, C₁-C₂₅alkyl, C₁-C₂₅alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by G, a C₄-C₁₈cycloalkyl group, a C₄-C₁₈cycloalkyl group, which is substituted by G, C₂-C₁₈alkenyl, C₂-C₁₈alkynyl, C₁-C₂₅alkylthio, C₁-C₂₅alkoxy, C₁-C₂₅alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, or C₇-C₂₅aralkyl, which is substituted by G,

R²⁷ and R²⁸ are independently of each other hydrogen, C₁-C₂₅alkyl, halogen, cyano or C₇-C₂₅aralkyl, or R²⁷ and R²⁸ together represent alkylene or alkenylene which may be both bonded via oxygen and/or sulfur to the thienyl residue and which may both have up to 25 carbon atoms,

R⁵⁹ is hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; or C₇-C₂₅arylalkyl,

R⁶⁰ is hydrogen, C₁-C₁₈haloalkyl, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₁-C₁₈alkanoyl, or C₇-C₂₅arylalkyl,

R¹⁰³ and R^(103′) are independently of each other hydrogen, C₁-C₁₀₀alkyl, C₁-C₂₅alkyl substituted by E and/or interrupted with D, C₂-C₂₅alkenyl, C₂-C₂₅alkenyl substituted by E and/or interrupted with D, C₇-C₂₅arylalkyl, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, C₂-C₂₀heteroaryl, or C₂-C₂₀heteroaryl which is substituted by G,

R¹⁰⁴ and R^(104′) are independently of each other hydrogen, CN, C₁-C₁₈alkyl, C₆-C₁₀aryl, which may optionally be substituted by G, or C₂-C₈heteroaryl, which may optionally be substituted by G,

R¹⁰⁵, R^(105′), R¹⁰⁶ and R^(106′) are independently of each other hydrogen, halogen, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₇-C₂₅arylalkyl, or C₁-C₁₈alkoxy,

R¹⁰⁷ is hydrogen, C₇-C₂₅arylalkyl, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₁₈perfluoroalkyl; C₁-C₂₅alkyl, which may be interrupted by —O—, or —S—; or —COOR¹⁰³; R¹⁰³ is as defined above;

R¹⁰⁸ and R¹⁰⁹ are independently of each other H, C₁-C₂₅alkyl, C₁-C₂₅alkyl which is substituted by E and/or interrupted by D, C₇-C₂₅arylalkyl, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by G, C₂-C₁₈alkenyl, C₂-C₁₈alkynyl, C₁-C₁₈alkoxy, C₁-C₁₈alkoxy which is substituted by E and/or interrupted by D, or C₇-C₂₅aralkyl, or

R¹⁰⁸ and R¹⁰⁹ together form a group of formula ═CR¹¹⁰R¹¹¹, wherein

R¹¹⁰ and R¹¹¹ are independently of each other H, C₁-C₁₈alkyl, C₁-C₁₈alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, or C₂-C₂₀heteroaryl, or C₂-C₂₀heteroaryl which is substituted by G, or

R¹⁰⁸ and R¹⁰⁹ together form a five or six membered ring, which optionally can be substituted by C₁-C₁₈alkyl, C₁-C₁₈alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by G, C₂-C₁₈alkenyl, C₂-C₁₈alkynyl, C₁-C₁₈alkoxy, C₁-C₁₈alkoxy which is substituted by E and/or interrupted by D, or C₇-C₂₅aralkyl,

D is —CO—, —COO—, —S—, —O—, or —NR¹¹²—,

E is C₁-C₁₈alkylthio, C₁-C₁₈alkoxy, CN, —NR¹¹²R¹¹³, —CONR¹¹²R¹¹³, or halogen,

G is E, or C₁-C₁₈alkyl, and

R¹¹² and R¹¹³ are independently of each other H; C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₁₈alkyl; or C₁-C₁₈alkyl which is interrupted by —O—,

R¹¹⁴ is C₁-C₂₅alkyl, which may optionally be interrupted by one, or more oxygen, or sulphur atoms,

R¹¹⁵ and R^(115′) are independently of each other hydrogen, halogen, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one, or more oxygen, or sulphur atoms, C₁-C₂₅alkoxy, C₇-C₂₅arylalkyl, or

R¹¹⁶ is a C₁-C₁₀alkyl group, or a tri(C₁-C₈alkyl)silyl group;

R¹¹⁷ and R^(117′) are independently of each other C₁-C₂₅alkyl group, especially a C₁-C₈alkyl group, C₇-C₂₅arylalkyl, or a phenyl group, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy;

R¹¹⁸, R¹¹⁹, R¹²⁰ and R¹²¹ are independently of each other hydrogen, halogen, halogenated C₁-C₂₅alkyl, especially CF₃, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₇-C₂₅arylalkyl, or C₁-C₂₅alkoxy;

R¹²² and R^(122′) are independently of each other hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; or C₇-C₂₅arylalkyl, and

R¹²⁴ and R^(124′) are independently of each other hydrogen, cyano, COOR¹⁰³, a C₁-C₂₅alkyl group, C₆-C₂₄aryl, or C₂-C₂₀heteroaryl,

E_(Si) is —SiR¹⁶¹R¹⁶²R¹⁶³ or —O—SiR¹⁶¹R¹⁶²R¹⁶³;

R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other hydrogen, C₁-C₂₅alkyl, C₃-C₁₂cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₂₅haloalkyl, C₂-C₂₅alkenyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶, C₁-C₂₅alkoxy, C₃-C₂₄(hetero)aryloxy, NR¹⁶⁷R¹⁶⁸, halogen, C₁-C₂₅acyloxy, phenyl, phenyl, which is substituted 1 to 3 times by C₁-C₂₄alkyl, halogen, cyano or C₁-C₂₅alkoxy;

R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other hydrogen, C₁-C₂₅alkyl, C₃-C₁₂cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₂₅haloalkyl, C₂-C₂₅alkenyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹, C₁-C₂₅alkoxy, C₃-C₂₄(hetero)aryloxy, NR¹⁶⁷R¹⁶⁸, halogen, C₁-C₂₅acyloxy, phenyl, phenyl which is substituted 1 to 3 times by C₁-C₂₄alkyl, halogen, cyano or C₁-C₂₅alkoxy;

R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other hydrogen, C₁-C₂₅alkyl, C₃-C₁₂cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₂₅haloalkyl, C₂-C₂₅alkenyl, —O—Si(CH₃)₃, C₁-C₂₅alkoxy, C₃-C₂₄(hetero)aryloxy, NR¹⁶⁷R¹⁶⁸, halogen, C₁-C₂₅acyloxy, phenyl, phenyl, which is substituted 1 to 3 times by C₁-C₂₄alkyl, halogen, cyano or C₁-C₂₅alkoxy;

R¹⁶⁷ and R¹⁶⁸ are independently of each other hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; or C₇-C₂₅arylalkyl;

d is an integer from 1 to 50;

R²¹⁴ and R²¹⁵ are independently of each other hydrogen, C₁-C₁₈alkyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, —CN or COOR²¹⁶; and

R²¹⁶ is C₁-C₂₅alkyl, C₁-C₂₅haloalkyl, C₇-C₂₅arylalkyl, C₆-C₂₄aryl or C₂-C₂₀heteroaryl.

The FIGURE shows representative transfer characteristics of an FET fabricated from polymer P9 with V_(GS)=10 V to −30 V at 0.5V step size with V_(DS)=−30V. Drain current (black solid curve), Gate current (dotted grey curve), Square root of drain current (grey solid curve), and fitted slope of square root (dashed black curve).

The compounds of formula (I) may be used as functional dyes in dye sensitized and bulk heterojunction solar cells, organic light-emitting diodes, photodiodes, organic field-effect transistors, fluorescence imaging, sensors and solid-state dye lasers.

The compounds of formula (I) may also show very strong fluorescence and two photon absorption. Owing to these features, these dyes are excellent candidates for application in such fields as: fluorescence imaging, detection of cations and colouring of artist's or industrial paints.

Y is preferably a group of formula

wherein T¹, T², T³, T⁴, U¹ and U² are defined above and below.

In a more preferred embodiment Y is a group of formula

especially a group of formula

wherein T¹, T², T³, T⁴, U¹ and U² are defined above and below.

In another more preferred embodiment Y is a group of formula

especially a group of formula

wherein T¹, T², T³, T⁴, U¹ and U² are defined above and below.

The compound of formula (I) is preferably a compound of formula

wherein T¹, T², T³, T⁴, U¹, U², Ar, Ar′, R¹⁰ and R^(10′) are defined above and below.

The compound of formula (I) is more preferably a compound of formula

or a compound of formula

wherein T¹, T², T³, T⁴, U¹, U², Ar, Ar′, R¹⁰ and R^(10′) are defined above and below.

T¹ and T² are preferably H, a C₁-C₃₈alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, cyano, or E_(Si); and/or can optionally be interrupted by —O—, —S—, or —NR⁶⁰—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy, wherein

E_(Si) is —SiR¹⁶¹R¹⁶²R¹⁶³;

R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other C₁-C₈alkyl, C₅-C₆cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶, or phenyl;

R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹, or phenyl;

R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—Si(CH₃)₃, or phenyl;

d is an integer from 1 to 10.

T³ and T⁴ are preferably H, a C₁-C₃₈alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, cyano, or E_(Si); and/or can optionally be interrupted by —O—, —S—, or —NR⁶⁰—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy, wherein E_(Si) is —SiR¹⁶¹R¹⁶²R¹⁶³;

R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other C₁-C₈alkyl, C₅-C₆cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶, or phenyl;

R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹, or phenyl;

R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—Si(CH₃)₃, or phenyl;

d is an integer from 1 to 10.

The compound of formula (Ia-1) is especially a compound of formula

The compound of formula (Ia-2) is especially a compound of formula

T¹, T², T³, T⁴, U¹, U², Ar, Ar′, R¹⁰ and R^(10′) are defined above.

U¹ and U² are preferably O.

Examples of the group of formula

are groups of formula

Examples of the group of formula

are groups of formula

Examples of the group of formula

are groups of formula

An example of the group of formula

is a group of formula

Examples of the group of formula

are groups of formula

Examples of the group of formula

are groups of formula

Ar¹, Ar¹′, Ar², Ar²′, Ar³ and Ar³′ are preferabl

wherein

R³ and R^(3′) are independently of each other hydrogen, F, C₁-C₂₅alkyl, or C₁-C₂₅alkoxy, R⁸ is hydrogen, or C₁-C₂₅alkyl, and R¹⁰⁴ and R^(104′) are independently of each other hydrogen, cyano, COOR¹⁰³, or a C₁-C₂₅alkyl group, wherein R¹⁰³ is a C₁-C₂₅alkyl group, which can optionally be interrupted by —O—, or —S—. Groups of formula (XIa-1), (XIa-2), (XIa-4), (XId), (XIf) and (XIv) are even more preferred.

—Ar—R¹⁰ and —Ar′—R^(10′) are preferably H, F, cyano, C₁-C₂₅alkyl, C₁-C₂₅alkyl substituted with one or more halogen atoms,

—Ar—R¹⁰ and —Ar′—R^(10′) are more preferably H, or

R³ and R^(3′) are independently of each other hydrogen, F, C₁-C₂₅alkyl, or C₁-C₂₅alkoxy, R²², R²³, R²⁵, R²⁶, R²⁷, R²⁸ and R²⁹ to R³³ represent independently of each other H, F, cyano, C₁-C₂₅alkoxy, C₁-C₂₅alkyl substituted with one or more F, C₁-C₂₅alkyl interrupted with one or more —O—, or C₁-C₂₅alkyl, and

R²⁴ is H, F, cyano, NO₂, NR¹¹²R¹¹³, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkylthio, C₁-C₂₅alkyl substituted with one or more halogen atoms (CF₃), C₁-C₂₅alkyl interrupted with one or more —O—, or C₁-C₂₅alkyl;

X is O, S, Se, or NR⁸, X⁵ is O, S, Se, or NR⁵⁹,

R⁵⁸ is H, F, cyano, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkylthio, C₁-C₂₅alkyl substituted with one or more halogen atoms (CF₃), or C₁-C₂₅alkyl;

R⁸ and R⁵⁹ are hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F; or C₇-C₂₅arylalkyl, R¹¹² and R¹¹³ are independently of each other hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F; or C₇-C₂₅arylalkyl.

In a particularly preferred embodiment the present invention is directed to compounds of formula

wherein

U¹ and U² are O,

T¹ and T² are H, a C₁-C₃₈alkyl group which can optionally be interrupted by —O—, —S—, or —NR⁶⁰—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy,

T³ and T⁴ are H, a C₁-C₃₈alkyl group which can optionally be interrupted by —O—, —S—, or —NR⁶⁰—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy, and

—Ar—R¹⁰ and —Ar′—R^(10′) are independently of each other H, F, cyano, C₁-C₂₅alkyl substituted with one or more fluorine atoms, C₁-C₂₅alkyl,

wherein R³ and R^(3′) are independently of each other hydrogen, F, C₁-C₂₅alkyl, or C₁-C₂₅alkoxy,

R²², R²³, R²⁵, R²⁶, R²⁷, R²⁸ and R²⁹ to R³³ represent independently of each other H, F, cyano, C₁-C₂₅alkoxy, C₁-C₂₅alkyl substituted with one or more F, C₁-C₂₅alkyl interrupted with one or more —O—, or C₁-C₂₅alkyl, and

R²⁴ is H, F, cyano, NO₂, NR¹¹²R¹¹³, CF₃, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkyl substituted with one or more halogen atoms, C₁-C₂₅alkyl interrupted with one or more —O—, or C₁-C₂₅alkyl;

X is O, S, Se, or NR⁸, X⁵ is O, S, Se, or NR⁵⁹,

R⁵⁸ is H, F, cyano, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkylthio, C₁-C₂₅alkyl substituted with one or more halogen atoms (CF₃), or C₁-C₂₅alkyl;

R⁸ and R⁵⁹ are hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F; or C₇-C₂₅arylalkyl, and

R¹¹² and R¹¹³ are independently of each other hydrogen, C₆-C₈aryl; C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F; or C₇-C₂₅arylalkyl.

In said embodiment T³ and T⁴ are preferably H and the present invention is preferably directed to compounds of formula (Ia-1a). T¹ and T² are preferably H, a C₁-C₃₈alkyl group, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy.

In another particularly preferred embodiment the present invention is directed to compounds of formula

wherein

U¹ and U² are O,

T¹ and T² are H, a C₁-C₃₈alkyl group which can optionally be interrupted by —O—, —S—, or —NR⁶⁰—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy,

T³ and T⁴ are H, a C₁-C₃₈alkyl group can optionally be interrupted by —O—, —S—, or —NR⁶⁰—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy, and

—Ar—R¹⁰ and —Ar′—R^(10′) are independently of each other H, F, cyano, C₁-C₂₅alkyl substituted with one or more fluorine atoms, C₁-C₂₅alkyl,

wherein R³ and R^(3′) are independently of each other hydrogen, F, C₁-C₂₅alkyl, or C₁-C₂₅alkoxy,

R²², R²³, R²⁵, R²⁶, R²⁷, R²⁸ and R²⁹ to R³³ represent independently of each other H, F, cyano, C₁-C₂₅alkoxy, C₁-C₂₅alkyl substituted with one or more F, C₁-C₂₅alkyl interrupted with one or more —O—, or C₁-C₂₅alkyl, and

R²⁴ is H, F, cyano, NO₂, NR¹¹²R¹¹³, CF₃, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkyl substituted with one or more halogen atoms, C₁-C₂₅alkyl interrupted with one or more —O—, or C₁-C₂₅alkyl;

X is O, S, Se, or NR⁸, X⁵ is O, S, Se, or NR⁵⁹,

R⁵⁸ is H, F, cyano, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkylthio, C₁-C₂₅alkyl substituted with one or more halogen atoms (CF₃), or C₁-C₂₅alkyl;

R⁸ and R⁵⁹ are hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁alkoxy; C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F; or C₇-C₂₅arylalkyl, and

R¹¹² and R¹¹³ are independently of each other hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F; or C₇-C₂₅arylalkyl.

In said embodiment T¹ and T² are preferably H and the present invention is preferably directed to compounds of formula (Ia-2a). T³ and T⁴ are preferably H, a C₁-C₃₈alkyl group, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy.

Examples of compounds of formula (I) are compounds (A-1) to (A-15) shown in claim 9 and compounds of formula

A process for producing compounds of formula

(a) reacting a compound of formula

with a compound of formula T¹COOH (XIIa) and T²COOH (XIIb), or T¹COOH (XIIa) in a solvent, such as, for example, dichloromethane, in the presence of an acid and/or an acid anhydride, such as, for example, trifluoroacetic acid and/or trifluoroacetic anhydride, wherein T¹, T², T³, T⁴, U¹, U², Ar, Ar′, R¹⁰ and R^(10′) are defined above and in case a compound of formula (XI) is reacted only with a compound of formula (XIIa) T² in formula (Ia) has the meaning of T¹. Instead of the acids T¹COOH (XIIa) and T²COOH (XIIb) their anhydrides, (T¹CO)₂O and (T²CO)₂O, may be used.

The compounds of formula (XI), (XIIa) and (XIIb) are commercially available, or can be prepared according to procedures known in the art.

Another process for producing compounds of formula

comprises

(a) reacting a compound of formula

or (XIIIa) with a compound of formula ClCO(CH₂)₂COCl (XIV) in a solvent, such as, for example, dimethylformamide (DMF), or dichloromethane, in the presence of a base, such as, for example, 4-dimethylaminopyridine, trimethylamine, or potassium carbonate, wherein T¹, T², T³, T⁴, U¹, U², Ar, Ar′, R¹⁰ and R^(10′) are defined above and in case a compound of formula (XIV) is reacted only with a compound of formula (XIIIa) T² in formula (Ia) has the meaning of T¹. The process can be used for the production of compounds of formula (Ia), wherein T¹ and T² are H, such as, for example, compound (A-1).

The compounds of formula (XIIIa), (XIIIa) and (XIV) are commercially available, or can be prepared according to procedures known in the art.

Compound (C-1) can, for example, be prepared starting from the compound (A-3) as shown in the reaction scheme below:

The bromination is carried out in a suitable solvent, like chloroform, using two equivalents of N-bromo-succinimide at a temperature between −30° C. and +50° C., preferably between −10° C. and room temperature, e.g. at 0° C.

Advantageously, the compound of formula I, or an organic semiconductor material, layer or component, comprising the compound of formula I can be used in organic photovoltaics (solar cells) and photodiodes, or in an organic field effect transistor (OFET).

A mixture containing the compound of formula I results in a semi-conducting layer comprising the compound of formula I (typically 0.1% to 99.9999% by weight, more specifically 1% to 99.9999% by weight, even more specifically 5% to 99.9999% by weight, especially 20 to 85% by weight) and at least another material. The other material can be, but is not restricted to another compound of formula I, a polymer of the present invention, a semi-conducting polymer, a non-conductive polymer, organic small molecules, carbon nanotubes, a fullerene derivative, inorganic particles (quantum dots, quantum rods, quantum tripods, TiO₂, ZnO etc.), conductive particles (Au, Ag etc.), insulator materials like the ones described for the gate dielectric (PET, PS etc.).

Accordingly, the present invention also relates to an organic semiconductor material, layer or component, comprising a compound of formula I and to a semiconductor device, comprising a compound of formula I and/or an organic semiconductor material, layer or component.

The semiconductor is preferably used in an organic photovoltaic (PV) device (solar cell), a photodiode, or an organic field effect transistor. The structure and the components of the OFET device has been described in more detail below.

Accordingly, the invention provides organic photovoltaic (PV) devices (solar cells) comprising a compound of the formula I.

The structure of organic photovoltaic devices (solar cells) is, for example, described in C. Deibel et al. Rep. Prog. Phys. 73 (2010) 096401 and Christoph Brabec, Energy Environ. Sci 2. (2009) 347-303.

The PV device comprise in this order:

(a) a cathode (electrode),

(b) optionally a transition layer, such as an alkali halogenide, especially lithium fluoride,

(c) a photoactive layer,

(d) optionally a smoothing layer,

(e) an anode (electrode),

(f) a substrate.

The photoactive layer comprises the compounds of the formula I. Preferably, the photoactive layer is made of a compound of the formula I, as an electron donor and an acceptor material, like a fullerene, particularly a functionalized fullerene PCBM, as an electron acceptor. As stated above, the photoactive layer may also contain a polymeric binder. The ratio of the small molecules of formula I to the polymeric binder can vary from 5 to 95 percent. Preferably, the polymeric binder is a semicrystalline polymer such as polystyrene (PS), high-density polyethylene (HDPE), polypropylene (PP) and polymethylmethacrylate (PMMA).

The fullerenes useful in this invention may have a broad range of sizes (number of carbon atoms per molecule). The term fullerene as used herein includes various cage-like molecules of pure carbon, including Buckminsterfullerene (C₆₀) and the related “spherical” fullerenes as well as carbon nanotubes. Fullerenes may be selected from those known in the art ranging from, for example, C₂₀-C₁₀₀₀. Preferably, the fullerene is selected from the range of C₆₀ to C₉₆. Most preferably the fullerene is C₆₀ or C₇₀, such as [60]PCBM, or [70]PCBM. It is also permissible to utilize chemically modified fullerenes, provided that the modified fullerene retains acceptor-type and electron mobility characteristics. The acceptor material can also be a material selected from the group consisting of another compounds of formula III, or any semi-conducting polymer, such as, for example, a polymer of formula I, provided that the polymers retain acceptor-type and electron mobility characteristics, organic small molecules, carbon nanotubes, inorganic particles (quantum dots, quantum rods, quantum tripods, TiO₂, ZnO etc.).

The photoactive layer is made of a compound of the formula I, as an electron donor and a fullerene, particularly functionalized fullerene PCBM, as an electron acceptor. These two components are mixed with a solvent and applied as a solution onto the smoothing layer by, for example, the spin-coating method, the drop casting method, the Langmuir-Blodgett (“LB”) method, the ink jet printing method and the dripping method. A squeegee or printing method could also be used to coat larger surfaces with such a photoactive layer. Instead of toluene, which is typical, a dispersion agent such as chlorobenzene is preferably used as a solvent. Among these methods, the vacuum deposition method, the spin-coating method, the ink jet printing method and the casting method are particularly preferred in view of ease of operation and cost.

In the case of forming the layer by using the spin-coating method, the casting method and ink jet printing method, the coating can be carried out using a solution and/or dispersion prepared by dissolving, or dispersing the composition in a concentration of from 0.01 to 90% by weight in an appropriate organic solvent such as benzene, toluene, xylene, tetrahydrofurane, methyltetrahydrofurane, N,N-dimethylformamide, acetone, acetonitrile, anisole, dichloromethane, dimethylsulfoxide, chlorobenzene, 1,2-dichlorobenzene and mixtures thereof.

The photovoltaic (PV) device can also consist of multiple junction solar cells that are processed on top of each other in order to absorb more of the solar spectrum. Such structures are, for example, described in App. Phys. Let. 90, 143512 (2007), Adv. Funct. Mater. 16, 1897-1903 (2006) and WO2004/112161.

A so called ‘tandem solar cell’ comprise in this order:

(a) a cathode (electrode),

(b) optionally a transition layer, such as an alkali halogenide, especially lithium fluoride,

(c) a photoactive layer,

(d) optionally a smoothing layer,

(e) a middle electrode (such as Au, Al, ZnO, TiO₂ etc.)

(f) optionally an extra electrode to match the energy level,

(g) optionally a transition layer, such as an alkali halogenide, especially lithium fluoride,

(h) a photoactive layer,

(i) optionally a smoothing layer,

(j) an anode (electrode),

(k) a substrate.

The PV device can also be processed on a fiber as described, for example, in US20070079867 and US 20060013549.

An OFET device according to the present invention preferably comprises:

-   -   a source electrode,     -   a drain electrode,     -   a gate electrode,     -   a semiconducting layer,     -   one or more gate insulator layers, and     -   optionally a substrate, wherein the semiconductor layer         comprises a compound of formula I.

The gate, source and drain electrodes and the insulating and semiconducting layer in the OFET device may be arranged in any sequence, provided that the source and drain electrode are separated from the gate electrode by the insulating layer, the gate electrode and the semiconductor layer both contact the insulating layer, and the source electrode and the drain electrode both contact the semiconducting layer.

Preferably the OFET comprises an insulator having a first side and a second side, a gate electrode located on the first side of the insulator, a layer comprising a compound of formula I located on the second side of the insulator, and a drain electrode and a source electrode located on the polymer layer.

The present invention is also directed to polymers, comprising a repeating unit of the formula —[(Ar)_(z) ¹—Y—(Ar′)_(z) ²]—  (V), wherein

z¹ and z² are independently of each other 0, or 1,

Y, Ar and Ar′ are defined above, or below.

The repeating unit of the formula (V) is preferably a repeating unit of formula

z¹ and z² are independently of each other 0, or 1 and T¹, T², T³, T⁴, U¹, U², Ar and Ar′ are defined above, or below.

In a more preferred embodiment the repeating unit of the formula (V) is a repeating unit of formula

especially a repeating unit of formula

wherein z1, z2, T¹, T², T³, T⁴, U¹, U², Ar and Ar′ are defined above and below.

In another more preferred embodiment the repeating unit of the formula (V) is a repeating unit of formula

especially a repeating unit of formula

wherein z1, z2, T¹, T², T³, T⁴, U¹, U², Ar and Ar′ are defined above and below.

U¹ and U² are preferably O.

Preferably T¹, T², T³ and T⁴ are independently of each other H, a C₁-C₃₈alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, or E_(Si); and/or can optionally be interrupted by —O—, or —S—; or a C₂-C₃₈alkenyl group which can optionally be substituted one or more times with C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, or E_(Si); and/or can optionally be interrupted by —O—, or —S—; wherein E_(Si) is —SiR¹⁶¹R¹⁶²R¹⁶³. More preferred, T¹, T², T³ and T⁴ are independently of each other H, a C₁-C₃₈alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, or E_(Si); and/or can optionally be interrupted by —O—, or —S—, wherein E_(Si) is —SiR¹⁶¹R¹⁶²R¹⁶³. Even more preferred, T¹, T², T³ and T⁴ are independently of each other H, or a C₁-C₃₈alkyl group, which can optionally be interrupted by —O—, or —S—. Most preferred T¹, T², T³ and T⁴ are H, or a C₁-C₃₈alkyl group.

R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other C₁-C₈alkyl, C₅-C₆cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶, or phenyl;

R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹, or phenyl;

R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—Si(CH₃)₃, or phenyl;

d is an integer from 1 to 10.

Preferably, R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other C₁-C₈alkyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, or —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶. Preferably, R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other C₁-C₈alkyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, or —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹. Preferably, R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other C₁-C₈alkyl or —O—Si(CH₃)₃. d is preferably an integer from 1 to 5.

—Ar— and —Ar′— are preferably a single bond,

wherein

R³ and R^(3′) are independently of each other hydrogen, F, C₁-C₂₅alkyl, or C₁-C₂₅alkoxy, R⁸ is hydrogen, or C₁-C₂₅alkyl, and R¹⁰⁴ and R^(104′) are independently of each other hydrogen, cyano, COOR¹⁰³, or a C₁-C₂₅alkyl group, wherein R¹⁰³ is a C₁-C₂₅alkyl group, which can optionally be interrupted by —O—, or —S—. R³ and R^(3′) are preferably hydrogen. Preferably, R¹⁰⁴ and R^(104′) are independently of each other hydrogen, or cyano, most preferred hydrogen.

Groups of formula (XIa-1), (XIa-2), (XIa-4), (XId), (XIf) and (XIv) are even more preferred.

In another embodiment the present invention is directed to polymers, comprising a repeating unit of the formula *

A

* and a repeating unit *

COM¹

*, wherein

A is a repeating unit of formula (V), and

—COM¹- is a repeating unit, which has the meaning of Ar², wherein Ar² is defined in claim 1, or a group of formula

s is 1, t is 1, u is 0, or 1, v is 0, or 1, and

Ar⁴ and Ar⁵ are independently of each other a group of formula

Ar¹⁴, Ar¹⁵, Ar¹⁶ and Ar¹⁷ are independently of each other a group of formula

wherein

one of X⁷ and X⁸ is N and the other is CR¹⁴,

R¹⁴, R^(14′), R¹⁷ and R^(17′) are independently of each other H, F, a C₁-C₂₅alkyl group, or a C₁-C₂₅alkoxy group,

R²⁰⁰ and R^(200′) are independently of each other H, or F,

R²⁰¹ and R²⁰² are independently of each other H, a C₁-C₁₀₀alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₂-C₁₀₀alkenyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—,

a C₃-C₁₀₀alkinyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—,

a C₃-C₁₂cycloalkyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—,

a C₆-C₂₄aryl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si);

a C₂-C₂₀heteroaryl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and E_(Si) is defined in claim 1,

R⁶⁰ is hydrogen, C₁-C₁₈haloalkyl, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₁-C₁₈alkanoyl, or C₇-C₂₅arylalkyl,

R²⁰⁶ is hydrogen, or C₁-C₂₅alkyl, or C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; and

R³⁰⁴ and R^(304′) are independently of each other hydrogen, cyano, COOR³⁰⁵, or a C₁-C₂₅alkyl group, wherein R³⁰⁵ is a C₁-C₂₅alkyl group, which can optionally be interrupted by —O—, or S—.

Ar⁴ and Ar⁵ are preferably a group of formula

R¹⁴, R^(14′), R¹⁷ and R^(17′) are preferably H.

Preferably, Ar¹⁴, Ar¹⁵, Ar¹⁶ and Ar¹⁷ are independently of each other a group of formula

E_(Si) is preferably —SiR¹⁶¹R¹⁶²R¹⁶³;

R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other C₁-C₈alkyl, C₅-C₆cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶, or phenyl;

R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹, or phenyl;

R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—Si(CH₃)₃, or phenyl;

d is an integer from 1 to 10.

Preferably, R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other C₁-C₈alkyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, or —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶. Preferably, R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other C₁-C₈alkyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, or —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹. Preferably, R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other C₁-C₈alkyl or —O—Si(CH₃)₃. d is preferably an integer from 1 to 5. Preferably, R²⁰¹ and R²⁰² are independently of each other H, a C₁-C₅₀alkyl group which can optionally be substituted one or more times with halogen, or E_(Si); and/or can optionally be interrupted by —O—, or —S—; or a C₂-C₅₀alkenyl group which can optionally be substituted one or more times with halogen, or E_(Si); and/or can optionally be interrupted by —O—, or —S—. More preferred, R²⁰¹ and R²⁰² are independently of each other a C₁-C₅₀alkyl group, which can optionally be interrupted by —O—, or —S—. Most preferred, R²⁰¹ and R²⁰² are a C₁-C₅₀alkyl group. Preferably, R³⁰⁴ and R^(304′) are independently of each other hydrogen, or cyano. More preferred R³⁰⁴ and R^(304′) are hydrogen.

Examples of polymers, comprising a repeating unit of formula (V) are polymers (P-1) to (P-10) shown in claim 16 and the polymers of formula

To prepare polymers corresponding to formula -[-[A]-[COM]-]_(n)- (VII) a dihalogenide of formula X⁶-A-X⁶ is reacted with an (equimolar) amount of a diboronic acid or diboronate corresponding to formula X^(6′)

COM¹

X^(6′); or a dihalogenide of formula X⁶

COM¹

X⁶ is reacted with an (equimolar) amount of a diboronic acid or diboronate corresponding to formula X^(6′)-A-X^(6′), wherein X⁶ is halogen, especially Cl, Br, or I, very especially Br, and X^(6′) is independently in each occurrence —B(OH)₂, —B(OY¹)₂,

wherein Y¹ is independently in each occurrence a C₁-C₁₀alkyl group and Y² is independently in each occurrence a C₂-C₁₀alkylene group, such as —CY³Y⁴—CY⁵Y⁶—, or —CY⁷Y⁸—CY⁹Y¹⁰—CY¹¹Y¹²—, wherein Y³, Y⁴, Y⁵, Y⁶, Y⁷, Y⁸, Y⁹, Y¹⁰, Y¹¹ and Y¹² are independently of each other hydrogen, or a C₁-C₁₀alkyl group, especially —C(CH₃)₂C(CH₃)₂—, —CH₂C(CH₃)₂CH₂—, or —C(CH₃)₂CH₂C(CH₃)₂—, and Y¹³ and Y¹⁴ are independently of each other hydrogen, or a C₁-C₁₀alkyl group, under the catalytic action of Pd and triphenylphosphine. The reaction is typically conducted at about 0° C. to 180° C. in an aromatic hydrocarbon solvent such as toluene, xylene. Other solvents such as dimethylformamide, dioxane, dimethoxyethan and tetrahydrofuran can also be used alone, or in mixtures with an aromatic hydrocarbon. An aqueous base, preferably sodium carbonate or bicarbonate, potassium phosphate, potassium carbonate or bicarbonate is used as activation agent for the boronic acid, boronate and as the HBr scavenger. A polymerization reaction may take 0.2 to 100 hours. Organic bases, such as, for example, tetraalkylammonium hydroxide, and phase transfer catalysts, such as, for example TBAB, can promote the activity of the boron (see, for example, Leadbeater & Marco; Angew. Chem. Int. Ed. Eng. 42 (2003) 1407 and references cited therein). Other variations of reaction conditions are given by T. I. Wallow and B. M. Novak in J. Org. Chem. 59 (1994) 5034-5037; and M. Remmers, M. Schulze, and G. Wegner in Macromol. Rapid Commun. 17 (1996) 239-252. Control of molecular weight is possible by using either an excess of dibromide, diboronic acid, or diboronate, or a chain terminator.

The process described in WO2010/136352 can, for example, be used for the preparation of polymers of formula (VII). The polymerisation is carried out in presence of

a) a catalyst/ligand system comprising a palladium catalyst and an organic phosphine or phosphonium compound,

b) a base,

c) a solvent or a mixture of solvents.

Preferred organic phosphines are selected from trisubstituted phosphines of formula

Cpd. R^(1″) R^(5″) R^(6″) R^(3″) R^(4″) PN-1 

H H H H PN-2  cyclohexyl H H H H PN-3  phenyl H H H H PN-4  adamantyl H H H H PN-5  cyclohexyl —OCH₃ H H H PN-6  cyclohexyl ¹⁾ ¹⁾ H H PN-7 

¹⁾ ¹⁾ H H PN-8  phenyl ¹⁾ ¹⁾ H H PN-9  adamantyl ¹⁾ ¹⁾ H H PN-10 cyclohexyl H H ²⁾ ²⁾ PN-11

H H ²⁾ ²⁾ PN-12 phenyl H H ²⁾ ²⁾ PN-13 adamantyl H H ²⁾ ²⁾ ¹⁾ R^(5″) and R^(6″) together form a ring 

  ²⁾ R^(3″) and R^(4″) together form a ring 

Examples of preferred catalysts include the following compounds:

palladium(II) acetylacetonate, palladium(0) dibenzylidene-acetone complexes, palladium(II) propionate,

Pd₂(dba)₃: [tris(dibenzylideneacetone) dipalladium(0)],

Pd(dba)₂: [bis(dibenzylideneacetone) palladium(0)],

Pd(PR₃)₂, wherein PR₃ is a trisubstituted phosphine of formula VI,

Pd(OAc)₂: [palladium(II) acetate], palladium(II) chloride, palladium(II) bromide, lithium tetrachloropalladate(II),

PdCl₂(PR₃)₂; wherein PR₃ is a trisubstituted phosphine of formula VI; palladium(0) diallyl ether complexes, palladium(II) nitrate,

PdCl₂(PhCN)₂: [dichlorobis(benzonitrile) palladium(II)],

PdCl₂(CH₃CN): [dichlorobis(acetonitrile) palladium(II)], and

PdCl₂(COD): [dichloro(1,5-cyclooctadiene) palladium(II)].

Especially preferred are PdCl₂, Pd₂(dba)₃, Pd(dba)₂, Pd(OAc)₂, or Pd(PR₃)₂. Most preferred are Pd₂(dba)₃ and Pd(OAc)₂.

The palladium catalyst is present in the reaction mixture in catalytic amounts. The term “catalytic amount” refers to an amount that is clearly below one equivalent of the (hetero)aromatic compound(s), preferably 0.001 to 5 mol-%, most preferably 0.001 to 1 mol-%, based on the equivalents of the (hetero)aromatic compound(s) used.

The amount of phosphines or phosphonium salts in the reaction mixture is preferably from 0.001 to 10 mol-%, most preferably 0.01 to 5 mol-%, based on the equivalents of the (hetero)aromatic compound(s) used. The preferred ratio of Pd:phosphine is 1:4.

The base can be selected from all aqueous and nonaqueous bases and can be inorganic, or organic. It is preferable that at least 1.5 equivalents of said base per functional boron group is present in the reaction mixture. Suitable bases are, for example, alkali and alkaline earth metal hydroxides, carboxylates, carbonates, fluorides and phosphates such as sodium and potassium hydroxide, acetate, carbonate, fluoride and phosphate or also metal alcoholates. It is also possible to use a mixture of bases. The base is preferably a lithium salt, such as, for example, lithium alkoxides (such as, for example, lithium methoxide and lithium ethoxide), lithium hydroxide, carboxylate, carbonate, fluoride and/or phosphate.

The at present most preferred base is aqueous LiOHxH₂O (monohydrate of LiOH) and (waterfree) LiOH.

The reaction is typically conducted at about 0° C. to 180° C., preferably from 20 to 160° C., more preferably from 40 to 140° C. and most preferably from 40 to 120° C. A polymerization reaction may take 0.1, especially 0.2 to 100 hours.

In a preferred embodiment of the present invention the solvent is THF, the base is LiOH*H₂O and the reaction is conducted at reflux temperature of THF (about 65° C.).

The solvent is for example selected from toluene, xylenes, anisole, THF, 2-methyltetrahydrofuran, dioxane, chlorobenzene, fluorobenzene or solvent mixtures comprising one or more solvents like e.g. THF/toluene and optionally water. Most preferred is THF, or THF/water.

Advantageously, the polymerisation is carried out in presence of

a) palladium(II) acetate, or Pd₂(dba)₃, (tris(dibenzylideneacetone)dipalladium(0)) and an organic phosphine PN-1 to PN-8,

b) LiOH, or LiOHxH₂O; and

c) THF, and optionally water. If the monohydrate of LiOH is used, no water needs to be added.

The palladium catalyst is present in an amount of preferably about 0.5 mol-%, based on the equivalents of the (hetero)aromatic compound(s) used. The amount of phosphines or phosphonium salts in the reaction mixture is preferably about 2 mol-%, based on the equivalents of the (hetero)aromatic compound(s) used. The preferred ratio of Pd:phosphine is about 1:4.

Preferably the polymerization reaction is conducted under inert conditions in the absence of oxygen. Nitrogen and more preferably argon are used as inert gases.

The process described in WO2010/136352 is suitable for large-scale applications, is readily accessible and convert starting materials to the respective polymers in high yield, with high purity and high selectivity. The process can provide polymers having weight average molecular weights of at least 10,000, more preferably at least 20,000, most preferably at least 30,000. The at present most preferred polymers have a weight average molecular weight of 30,000 to 80,000 Daltons. Molecular weights are determined according to high-temperature gel permeation chromatography (HT-GPC) using polystyrene standards. The polymers preferably have a polydispersibility of 1.01 to 10, more preferably 1.1 to 3.0, most preferred 1.5 to 2.5.

If desired, a monofunctional aryl halide or aryl boronate, such as, for example,

may be used as a chain-terminator in such reactions, which will result in the formation of a terminal aryl group.

It is possible to control the sequencing of the monomeric units in the resulting copolymer by controlling the order and composition of monomer feeds in the Suzuki reaction.

The polymers of the present invention can also be sythesized by the Stille coupling (see, for example, Babudri et al, J. Mater. Chem., 2004, 14, 11-34; J. K. Stille, Angew. Chemie Int. Ed. Engl. 1986, 25, 508). To prepare polymers corresponding to formula VII a dihalogenide of formula X⁶-A-X⁶ is reacted with a compound of formula X^(6′)

COM¹

X^(6′), or a dihalogenide of formula X⁶

COM¹

X⁶ is reacted with a compound of formula X^(6′)-A-X⁶, wherein X^(6′) is a group —SnR²⁰⁷R²⁰⁸R²⁰⁹ and X⁶ is as defined above, in an inert solvent at a temperature in range from 0° C. to 200° C. in the presence of a palladium-containing catalyst, wherein R²⁰⁷, R²⁰⁸ and R²⁰⁹ are identical or different and are H or C₁-C₆alkyl, wherein two groups optionally form a common ring and these radicals are branched or unbranched. It must be ensured here that the totality of all monomers used has a highly balanced ratio of organotin functions to halogen functions. In addition, it may prove advantageous to remove any excess reactive groups at the end of the reaction by end-capping with monofunctional reagents. In order to carry out the process, the tin compounds and the halogen compounds are preferably introduced into one or more inert organic solvents and stirred at a temperature of from 0 to 200° C., preferably from 30 to 170° C. for a period of from 1 hour to 200 hours, preferably from 5 hours to 150 hours. The crude product can be purified by methods known to the person skilled in the art and appropriate for the respective polymer, for example repeated re-precipitation or even by dialysis.

Suitable organic solvents for the process described are, for example, ethers, for example diethyl ether, dimethoxyethane, diethylene glycol dimethyl ether, tetrahydrofuran, dioxane, dioxolane, diisopropyl ether and tert-butyl methyl ether, hydrocarbons, for example hexane, isohexane, heptane, cyclohexane, benzene, toluene and xylene, alcohols, for example methanol, ethanol, 1-propanol, 2-propanol, ethylene glycol, 1-butanol, 2-butanol and tertbutanol, ketones, for example acetone, ethyl methyl ketone and isobutyl methyl ketone, amides, for example dimethylformamide (DMF), dimethylacetamide and N-methylpyrrolidone, nitriles, for example acetonitrile, propionitrile and butyronitrile, and mixtures thereof.

The palladium and phosphine components should be selected analogously to the description for the Suzuki variant.

Alternatively, the polymers of the present invention can also be synthesized by the Negishi reaction using a zinc reagent A-(ZnX¹²)₂, wherein X¹² is halogen and halides, and COM¹-(X^(6′))₂, wherein X^(6′) is halogen or triflate, or using A-(X^(6′))₂ and COM¹-(ZnX¹²)₂. Reference is, for example, made to E. Negishi et al., Heterocycles 18 (1982) 117-22.

Alternatively, the polymers of the present invention can also be synthesized by the Hiyama reaction using a organosilicon reagent A-(SiR²¹⁰R²¹¹R²¹²)₂, wherein R²¹⁰, R²¹¹ and R²¹² are identical or different and are halogen, or C₁-C₆alkyl, and COM¹-(X^(6′))₂, wherein X^(6′) is halogen or triflate, or using A-(X^(6′))₂ and COM¹-(SiR²¹⁰R²¹¹R²¹²)₂. Reference is, for example, made to T. Hiyama et al., Pure Appl. Chem. 66 (1994) 1471-1478 and T. Hiyama et al., Synlett (1991) 845-853.

Alternatively, the polymers of the present invention can also be synthesized by the direct arylation polymerization reaction using a monomer A-(H)₂, and COM¹-(X^(6′))₂, wherein X^(6′) is halogen, or using A-(X^(6′))₂ and COM¹-(H)₂ wherein X^(6′) is halogen. Reference is, for example, made to P. Homyak et al., Macromolecules 2015, 48, 6978-6986, T. Nakanishi et al., J. Mater. Chem. A, 2015, 3, 4229-4238, or J. Kuwabara, Journal of Polymer Science, Part A: Polymer Chemistry 2016, 54, 2337-2345.

In another embodiment the present invention is directed to homopolymers of the type (A)_(n). Homopolymers of the type (A)_(n) can be obtained via Yamamoto coupling of dihalides X⁶-A-X⁶, where X⁶ is halogen, especially Cl, Br, or I, very especially Br. Alternatively homopolymers of the type (A)_(n) can be obtained via oxidative polymerization of units X⁶-A-X⁶, where X⁶ is hydrogen, e.g. with FeCl₃ as oxidizing agent.

Compounds of formula X⁶—Ar—Y—Ar′—X^(6′) (X) are new, intermediates in the production of the polymer of the present invention and form a further subject of the present invention.

Y, Ar and Ar′ are defined in claim 1, and

X⁶ and X^(6′) are independently of each other halogen, especially Cl, Br, or I, very especially Br, or I, ZnX¹², —SnR²⁰⁷R²⁰⁸R²⁰⁹, wherein R²⁰⁷, R²⁰⁸ and R²⁰⁹ are identical or different and are H, or C₁-C₆alkyl, wherein two radicals optionally form a common ring and these radicals are optionally branched or unbranched and X¹² is a halogen atom; or —OS(O)₂CF₃, —OS(O)₂-aryl, —OS(O)₂CH₃, —B(OH)₂, —B(OY¹)₂,

—BF₄Na, or —BF₄K, wherein Y¹ is independently in each occurrence a C₁-C₁₀alkyl group, and Y² is independently in each occurrence a C₂-C₁₀alkylene group, which can optionally be substituted by one, or more C₁-C₈alkyl groups, such as —CY³Y⁴—CY⁵Y⁶—, or —CY⁷Y⁸—CY⁹Y¹⁰—CY¹¹Y¹²—, wherein Y³, Y⁴, Y⁵, Y⁶, Y⁷, Y⁸, Y⁹, Y¹⁰, Y¹¹ and Y¹² are independently of each other hydrogen, or a C₁-C₁₀alkyl group, especially —C(CH₃)₂C(CH₃)₂—, —CH₂C(CH₃)₂CH₂—, or —C(CH₃)₂CH₂C(CH₃)₂—, and Y¹³ and Y¹⁴ are independently of each other hydrogen, or a C₁-C₁₀alkyl group.

Examples of compounds of formula (X) are compounds (C-1) to (C-5) shown in claim 23 and the compound of formula

In the context of the present invention, the terms halogen, C₁-C₂₅alkyl (C₁-C₁₈alkyl), C₂-C₂₅alkenyl (C₂-C₁₈alkenyl), C₂₋₂₅alkynyl (C₂₋₁₈alkynyl), aliphatic groups, aliphatic hydrocarbon groups, alkylene, alkenylene, cycloaliphatic hydrocarbon groups, cycloalkyl, cycloalkenyl groups, C₁-C₂₅alkoxy (C₁-C₁₈alkoxy), C₁-C₁₈perfluoroalkyl, carbamoyl groups, C₆-C₂₄aryl (C₆-C₁₈aryl), C₇-C₂₅aralkyl and heteroaryl are each defined as follows—unless stated otherwise:

Halogen is fluorine, chlorine, bromine and iodine, especially fluorine.

C₁-C₂₅alkyl (C₁-C₁₈alkyl) is typically linear or branched, where possible. Examples are methyl, ethyl, n-propyl, isopropyl, n-butyl, sec.-butyl, isobutyl, tert.-butyl, n-pentyl, 2-pentyl, 3-pentyl, 2,2-dimethylpropyl, 1,1,3,3-tetramethylpentyl, n-hexyl, 1-methylhexyl, 1,1,3,3,5,5-hexamethylhexyl, n-heptyl, isoheptyl, 1,1,3,3-tetramethylbutyl, 1-methylheptyl, 3-methylheptyl, n-octyl, 1,1,3,3-tetramethylbutyl and 2-ethylhexyl, n-nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, eicosyl, heneicosyl, docosyl, tetracosyl or pentacosyl. C₁-C₈alkyl is typically methyl, ethyl, n-propyl, isopropyl, n-butyl, sec.-butyl, isobutyl, tert.-butyl, n-pentyl, 2-pentyl, 3-pentyl, 2,2-dimethyl-propyl, n-hexyl, n-heptyl, n-octyl, 1,1,3,3-tetramethylbutyl and 2-ethylhexyl. C₁-C₄alkyl is typically methyl, ethyl, n-propyl, isopropyl, n-butyl, sec.-butyl, isobutyl, tert.-butyl.

Halogenated C₁-C₂₅alkyl (C₁-C₂₅haloalkyl) is a C₁-C₂₅alkyl group, where a part or all of the hydrogen atoms are replaced by halogen atoms, such as, for example, CF₃.

C₂-C₂₅alkenyl (C₂-C₁₈alkenyl) groups are straight-chain or branched alkenyl groups, such as e.g. vinyl, allyl, methallyl, isopropenyl, 2-butenyl, 3-butenyl, isobutenyl, n-penta-2,4-dienyl, 3-methyl-but-2-enyl, n-oct-2-enyl, n-dodec-2-enyl, isododecenyl, n-dodec-2-enyl or n-octadec-4-enyl.

C₂₋₂₅alkynyl (C₂-C₁₈alkynyl) is straight-chain or branched and preferably C₂₋₈alkynyl, which may be unsubstituted or substituted, such as, for example, ethynyl, 1-propyn-3-yl, 1-butyn-4-yl, 1-pentyn-5-yl, 2-methyl-3-butyn-2-yl, 1,4-pentadiyn-3-yl, 1,3-pentadiyn-5-yl, 1-hexyn-6-yl, cis-3-methyl-2-penten-4-yn-1-yl, trans-3-methyl-2-penten-4-yn-1-yl, 1,3-hexadiyn-5-yl, 1-octyn-8-yl, 1-nonyn-9-yl, 1-decyn-10-yl, or 1-tetracosyn-24-yl.

C₁₋₂₅alkanoyl (C₂₋₁₈alkanoyl) refers to a group R^(w)—(C═O)—, with R^(w) is C₁₋₂₅alkyl (C₁₋₁₈alkyl). Specific examples thereof include an acetyl group, a n-propanoyl group, an isopropanoyl group, a n-butyroyl group, and a tert-butyroyl group.

Alkylene is bivalent alkyl, i.e. alkyl having two (instead of one) free valencies, e.g. trimethylene or tetramethylene.

Alkenylene is bivalent alkenyl, i.e. alkenyl having two (instead of one) free valencies, e.g. —CH₂—CH═CH—CH₂—.

A cycloalkyl-alkyl group is an alkyl group substituted by a cycloalkyl group, e.g. cyclohexyl-methyl.

A group of the formula IV wherein two groups R²² to R²⁶ which are in the neighborhood of each other, together represent alkylene or alkenylene having up to 8 carbon atoms, thereby forming a ring, is e.g. a group of the formula

wherein in the group of the formula XXXII R²³ and R²⁴ together represent 1,4-butylene and in the group of the formula XXXIII R²³ and R²⁴ together represent 1,4-but-2-en-ylene.

C₁-C₂₅alkoxy groups (C₁-C₁₈alkoxy groups) are straight-chain or branched alkoxy groups, e.g. methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec-butoxy, tert-butoxy, amyloxy, isoamyloxy or tert-amyloxy, heptyloxy, octyloxy, isooctyloxy, nonyloxy, decyloxy, undecyloxy, dodecyloxy, tetradecyloxy, pentadecyloxy, hexadecyloxy, heptadecyloxy and octadecyloxy. Examples of C₁-C₈alkoxy are methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec.-butoxy, isobutoxy, tert.-butoxy, n-pentoxy, 2-pentoxy, 3-pentoxy, 2,2-dimethylpropoxy, n-hexoxy, n-heptoxy, n-octoxy, 1,1,3,3-tetramethylbutoxy and 2-ethylhexoxy, preferably C₁-C₄alkoxy such as typically methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec.-butoxy, isobutoxy, tert.-butoxy. The term “C₁-C₂₅alkylthio group” means the same groups as the alkoxy groups, except that the oxygen atom of the ether linkage is replaced by a sulfur atom.

C₁-C₁₈perfluoroalkyl, especially C₁-C₄perfluoroalkyl, is a branched or unbranched radical such as for example —CF₃, —CF₂CF₃, —CF₂CF₂CF₃, —CF(CF₃)₂, —(CF₂)₃CF₃, and —C(CF₃)₃.

A C₃-C₁₂cycloalkyl, or C₄-C₁₂cycloalkyl group is typically a C₅-C₁₂cycloalkyl group, such as, for example, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl, cyclododecyl, preferably cyclopentyl, cyclohexyl, cycloheptyl, or cyclooctyl, which may be unsubstituted or substituted. The cycloalkyl group, in particular a cyclohexyl group, can be condensed one or two times by phenyl which can be substituted one to three times with C₁-C₄-alkyl, halogen and cyano. Examples of such condensed cyclohexyl groups are:

in particular

wherein R¹⁵¹, R¹⁵², R¹⁵³, R¹⁵⁴, R¹⁵⁵ and R¹⁵⁶ are independently of each other C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen and cyano, in particular hydrogen.

C₆-C₂₄aryl (C₆-C₁₈aryl) is typically phenyl, indenyl, azulenyl, naphthyl, biphenyl, as-indacenyl, s-indacenyl, acenaphthylenyl, fluorenyl, phenanthryl, fluoranthenyl, triphenlenyl, chrysenyl, naphthacen, picenyl, perylenyl, pentaphenyl, hexacenyl, pyrenyl, or anthracenyl, preferably phenyl, 1-naphthyl, 2-naphthyl, 4-biphenyl, 9-phenanthryl, 2- or 9-fluorenyl, 3- or 4-biphenyl, which may be unsubstituted or substituted. Examples of C₆-C₁₂aryl are phenyl, 1-naphthyl, 2-naphthyl, 3- or 4-biphenyl, 2- or 9-fluorenyl or 9-phenanthryl, which may be unsubstituted or substituted.

C₇-C₂₅aralkyl is typically benzyl, 2-benzyl-2-propyl, β-phenyl-ethyl, α,α-dimethylbenzyl, ω-phenyl-butyl, ω,ω-dimethyl-ω-phenyl-butyl, ω-phenyl-dodecyl, ω-phenyl-octadecyl, ω-phenyl-eicosyl or ω-phenyl-docosyl, preferably C₇-C₁₈aralkyl such as benzyl, 2-benzyl-2-propyl, β-phenyl-ethyl, α,α-dimethylbenzyl, ω-phenyl-butyl, ω,ω-dimethyl-ω-phenyl-butyl, ω-phenyl-dodecyl or ω-phenyl-octadecyl, and particularly preferred C₇-C₁₂aralkyl such as benzyl, 2-benzyl-2-propyl, β-phenyl-ethyl, α,α-dimethylbenzyl, ω-phenyl-butyl, or ω,ω-dimethyl-ω-phenyl-butyl, in which both the aliphatic hydrocarbon group and aromatic hydrocarbon group may be unsubstituted or substituted. Preferred examples are benzyl, 2-phenylethyl, 3-phenylpropyl, naphthylethyl, naphthylmethyl, and cumyl.

Heteroaryl is typically C₂-C₂₀heteroaryl, i.e. a ring with five to seven ring atoms or a condensed ring system, wherein nitrogen, oxygen or sulfur are the possible hetero atoms, and is typically an unsaturated heterocyclic group with five to 30 atoms having at least six conjugated π-electrons such as thienyl, benzo[b]thienyl, dibenzo[b,d]thienyl, thianthrenyl, furyl, furfuryl, 2H-pyranyl, benzofuranyl, isobenzofuranyl, dibenzofuranyl, phenoxythienyl, pyrrolyl, imidazolyl, pyrazolyl, pyridyl, bipyridyl, triazinyl, pyrimidinyl, pyrazinyl, pyridazinyl, indolizinyl, isoindolyl, indolyl, indazolyl, purinyl, quinolizinyl, chinolyl, isochinolyl, phthalazinyl, naphthyridinyl, chinoxalinyl, chinazolinyl, cinnolinyl, pteridinyl, carbazolyl, carbolinyl, benzotriazolyl, benzoxazolyl, phenanthridinyl, acridinyl, pyrimidinyl, phenanthrolinyl, phenazinyl, isothiazolyl, phenothiazinyl, isoxazolyl, thienothienyl, furazanyl or phenoxazinyl, which can be unsubstituted or substituted.

Possible substituents of the above-mentioned groups are C₁-C₈alkyl, a hydroxyl group, a mercapto group, C₁-C₈alkoxy, C₁-C₈alkylthio, halogen, halo-C₁-C₈alkyl, a cyano group, a carbamoyl group, a nitro group or a silyl group, especially C₁-C₈alkyl, C₁-C₈alkoxy, C₁-C₈alkylthio, halogen, halo-C₁-C₈alkyl, or a cyano group.

C₁-C₂₅alkyl interrupted by one or more O is, for example, (CH₂CH₂O)₁₋₉—R^(x), where R^(x) is H or C₁-C₁₀alkyl, CH₂—CH(OR^(y′))—CH₂—O—R^(y), where R^(y) is C₁-C₁₈alkyl, and R^(y′) embraces the same definitions as R^(y) or is H.

C₁-C₂₅alkyl interrupted by one or more S is, for example, (CH₂CH₂S)₁₋₉—R^(x), where R^(x) is H or C₁-C₁₀alkyl, CH₂—CH(SR^(y′))—CH₂—S—R^(y), where R^(y) is C₁-C₁₈alkyl, and R^(y′) embraces the same definitions as R^(y) or is H.

If a substituent, such as, for example T³, occurs more than one time in a group, it can be different in each occurrence.

A mixture containing a polymer of the present invention results in a semi-conducting layer comprising a polymer of the present invention (typically 5% to 99.9999% by weight, especially 20 to 85% by weight) and at least another material. The other material can be, but is not restricted to a fraction of the same polymer of the present invention with different molecular weight, another polymer of the present invention, a semi-conducting polymer, organic small molecules, carbon nanotubes, a fullerene derivative, inorganic particles (quantum dots, quantum rods, quantum tripods, TiO₂, ZnO etc.), conductive particles (Au, Ag etc.), insulator materials like the ones described for the gate dielectric (PET, PS etc.).

The polymers of the present invention can be blended with compounds of formula (I) according to the present invention, or small molecules described, for example, in WO2009/047104, WO2010108873, WO009/047104, U.S. Pat. No. 6,690,029, WO2007082584, and WO2008107089.

The polymer can contain a small molecule, or a mixture of two, or more small molecule compounds.

Accordingly, the present invention also relates to an organic semiconductor material, layer or component, comprising a polymer according to the present invention.

The polymers of the invention can be used as the semiconductor layer in semiconductor devices. Accordingly, the present invention also relates to semiconductor devices, comprising a polymer of the present invention, or an organic semiconductor material, layer or component. The semiconductor device is especially an organic photovoltaic (PV) device (solar cell), a photodiode, or an organic field effect transistor.

The polymers of the invention can be used alone or in combination as the organic semiconductor layer of the semiconductor device. The layer can be provided by any useful means, such as, for example, vapor deposition (for materials with relatively low molecular weight) and printing techniques. The compounds of the invention may be sufficiently soluble in organic solvents and can be solution deposited and patterned (for example, by spin coating, dip coating, ink jet printing, gravure printing, flexo printing, offset printing, screen printing, microcontact (wave)-printing, drop or zone casting, or other known techniques).

The polymers of the invention can be used in integrated circuits comprising a plurality of OTFTs, as well as in various electronic articles. Such articles include, for example, radiofrequency identification (RFID) tags, backplanes for flexible displays (for use in, for example, personal computers, cell phones, or handheld devices), smart cards, medical devices, memory devices, sensors (e.g. light-, image-, bio-, chemo-, mechanical- or temperature sensors), especially photodiodes, or security devices and the like.

A further aspect of the present invention is an organic semiconductor material, layer or component comprising one or more polymers of the present invention. A further aspect is the use of the polymers or materials of the present invention in an organic photovoltaic (PV) device (solar cell), a photodiode, or an organic field effect transistor (OFET). A further aspect is an organic photovoltaic (PV) device (solar cell), a photodiode, or an organic field effect transistor (OFET) comprising a polymer or material of the present invention.

The polymers of the present invention are typically used as organic semiconductors in form of thin organic layers or films, preferably less than 30 microns thick. Typically the semiconducting layer of the present invention is at most 1 micron (=1 μm) thick, although it may be thicker if required. For various electronic device applications, the thickness may also be less than about 1 micron thick. For example, for use in an OFET the layer thickness may typically be 100 nm or less. The exact thickness of the layer will depend, for example, upon the requirements of the electronic device in which the layer is used.

For example, the active semiconductor channel between the drain and source in an OFET may comprise a layer of the present invention.

An OFET device according to the present invention preferably comprises:

-   -   a source electrode,     -   a drain electrode,     -   a gate electrode,     -   a semiconducting layer,     -   one or more gate insulator layers, and     -   optionally a substrate, wherein the semiconductor layer         comprises one or more polymers of the present invention.

The gate, source and drain electrodes and the insulating and semiconducting layer in the OFET device may be arranged in any sequence, provided that the source and drain electrode are separated from the gate electrode by the insulating layer, the gate electrode and the semiconductor layer both contact the insulating layer, and the source electrode and the drain electrode both contact the semiconducting layer.

Preferably, the OFET comprises an insulator having a first side and a second side, a gate electrode located on the first side of the insulator, a layer comprising a polymer of the present invention located on the second side of the insulator, and a drain electrode and a source electrode located on the polymer layer.

The OFET device can be a top gate device or a bottom gate device.

Suitable structures and manufacturing methods of an OFET device are known to the person skilled in the art and are described in the literature, for example in WO03/052841.

The gate insulator layer may comprise for example a fluoropolymer, like e.g. the commercially available Cytop 809M®, or Cytop 107M® (from Asahi Glass). Preferably the gate insulator layer is deposited, e.g. by spin-coating, doctor blading, wire bar coating, spray or dip coating or other known methods, from a formulation comprising an insulator material and one or more solvents with one or more fluoro atoms (fluorosolvents), preferably a perfluorosolvent. A suitable perfluorosolvent is e.g. FC75® (available from Acros, catalogue number 12380). Other suitable fluoropolymers and fluorosolvents are known in prior art, like for example the perfluoropolymers Teflon AF® 1600 or 2400 (from DuPont), or Fluoropel® (from Cytonix) or the perfluorosolvent FC 43® (Acros, No. 12377).

The semiconducting layer comprising a polymer of the present invention may additionally comprise at least another material. The other material can be, but is not restricted to another polymer of the present invention, a semi-conducting polymer, a polymeric binder, organic small molecules different from a polymer of the present invention, carbon nanotubes, a fullerene derivative, inorganic particles (quantum dots, quantum rods, quantum tripods, TiO₂, ZnO etc.), conductive particles (Au, Ag etc.), and insulator materials like the ones described for the gate dielectric (PET, PS etc.). As stated above, the semiconductive layer can also be composed of a mixture of one or more polymers of the present invention and a polymeric binder. The ratio of the polymers of the present invention to the polymeric binder can vary from 5 to 95 percent. Preferably, the polymeric binder is a semicrystalline polymer such as polystyrene (PS), high-density polyethylene (HDPE), polypropylene (PP) and polymethylmethacrylate (PMMA). With this technique, a degradation of the electrical performance can be avoided (cf. WO2008/001123A1).

The polymers of the present invention are advantageously used in organic photovoltaic (PV) devices (solar cells). Accordingly, the invention provides PV devices comprising a polymer according to the present invention. A device of this construction will also have rectifying properties so may also be termed a photodiode. Photoresponsive devices have application as solar cells which generate electricity from light and as photodetectors which measure or detect light.

The PV device comprise in this order:

(a) a cathode (electrode),

(b) optionally a transition layer, such as an alkali halogenide, especially lithium fluoride,

(c) a photoactive layer,

(d) optionally a smoothing layer,

(e) an anode (electrode),

(f) a substrate.

The photoactive layer comprises the polymers of the present invention. Preferably, the photoactive layer is made of a conjugated polymer of the present invention, as an electron donor and an acceptor material, like a fullerene, particularly a functionalized fullerene PCBM, as an electron acceptor. As stated above, the photoactive layer may also contain a polymeric binder. The ratio of the polymers of formula (V) to the polymeric binder can vary from 5 to 95 percent. Preferably, the polymeric binder is a semicrystalline polymer such as polystyrene (PS), high-density polyethylene (HDPE), polypropylene (PP) and polymethylmethacrylate (PMMA).

For heterojunction solar cells the active layer comprises preferably a mixture of a polymer of the present invention and a fullerene, such as [60]PCBM (=6,6-phenyl-C₆₁-butyric acid methyl ester), or [70]PCBM, in a weight ratio of 1:1 to 1:3. The fullerenes useful in this invention may have a broad range of sizes (number of carbon atoms per molecule). The term fullerene as used herein includes various cage-like molecules of pure carbon, including Buckminsterfullerene (C₆₀) and the related “spherical” fullerenes as well as carbon nanotubes. Fullerenes may be selected from those known in the art ranging from, for example, C₂₀-C₁₀₀₀. Preferably, the fullerene is selected from the range of C₆₀ to C₉₆. Most preferably the fullerene is C₆₀ or C₇₀, such as [60]PCBM, or [70]PCBM. It is also permissible to utilize chemically modified fullerenes, provided that the modified fullerene retains acceptor-type and electron mobility characteristics. The acceptor material can also be a material selected from the group consisting of any semi-conducting polymer, such as, for example, a polymer of the present invention, provided that the polymers retain acceptor-type and electron mobility characteristics, organic small molecules, carbon nanotubes, inorganic particles (quantum dots, quantum rods, quantum tripods, TiO₂, ZnO etc.).

The photoactive layer is made of a polymer of the present invention as an electron donor and a fullerene, particularly functionalized fullerene PCBM, as an electron acceptor. These two components are mixed with a solvent and applied as a solution onto the smoothing layer by, for example, the spin-coating method, the drop casting method, the Langmuir-Blodgett (“LB”) method, the ink jet printing method and the dripping method. A squeegee or printing method could also be used to coat larger surfaces with such a photoactive layer. Instead of toluene, which is typical, a dispersion agent such as chlorobenzene is preferably used as a solvent. Among these methods, the vacuum deposition method, the spin-coating method, the ink jet printing method and the casting method are particularly preferred in view of ease of operation and cost.

In the case of forming the layer by using the spin-coating method, the casting method and ink jet printing method, the coating can be carried out using a solution and/or dispersion prepared by dissolving, or dispersing the composition in a concentration of from 0.01 to 90% by weight in an appropriate organic solvent such as benzene, toluene, xylene, tetrahydrofurane, methyltetrahydrofurane, N,N-dimethylformamide, acetone, acetonitrile, anisole, dichloromethane, dimethylsulfoxide, chlorobenzene, 1,2-dichlorobenzene and mixtures thereof.

The photovoltaic (PV) device can also consist of multiple junction solar cells that are processed on top of each other in order to absorb more of the solar spectrum. Such structures are, for example, described in App. Phys. Let. 90, 143512 (2007), Adv. Funct. Mater. 16, 1897-1903 (2006) and WO2004/112161.

A so called ‘tandem solar cell’ comprise in this order:

(a) a cathode (electrode),

(b) optionally a transition layer, such as an alkali halogenide, especially lithium fluoride,

(c) a photoactive layer,

(d) optionally a smoothing layer,

(e) a middle electrode (such as Au, Al, ZnO, TiO₂ etc.)

(f) optionally an extra electrode to match the energy level,

(g) optionally a transition layer, such as an alkali halogenide, especially lithium fluoride,

(h) a photoactive layer,

(i) optionally a smoothing layer,

(j) an anode (electrode),

(k) a substrate.

The PV device can also be processed on a fiber as described, for example, in US20070079867 and US 20060013549.

The following examples are included for illustrative purposes only and do not limit the scope of the claims. Unless otherwise stated, all parts and percentages are by weight.

Weight-average molecular weight (Mw) and polydispersity (Mw/Mn=PD) are determined by Heat Temperature Gel Permeation Chromatography (HT-GPC) [Apparatus: GPC PL 220 from Polymer laboratories (Church Stretton, UK; now Varian) yielding the responses from refractive index (RI), Chromatographic conditions: Column: 3 “PLgel Olexis” column from Polymer Laboratories (Church Stretton, UK); with an average particle size of 13 im (dimensions 300×8 mm I.D.) Mobile phase: 1,2,4-trichlorobenzene purified by vacuum distillation and stabilised by butylhydroxytoluene (BHT, 200 mg/l), Chromatographic temperature: 150° C.; Mobile phase flow: 1 ml/min; Solute concentration: about 1 mg/ml; Injection volume: 200 il; Detection: RI, Procedure of molecular weight calibration: Relative calibration is done by use of a set of 10 polystyrene calibration standards obtained from Polymer Laboratories (Church Stretton, UK) spanning the molecular weight range from 1,930,000 Da-5,050 Da, i.e., PS 1,930,000, PS 1,460,000, PS 1,075,000, PS 560,000, PS 330,000, PS 96,000, PS 52,000, PS 30,300, PS 10,100, PS 5,050 Da. A polynomic calibration is used to calculate the molecular weight.

All polymer structures given in the examples below are idealized representations of the polymer products obtained via the polymerization procedures described. If more than two components are copolymerized with each other sequences in the polymers can be either alternating or random depending on the polymerisation conditions.

EXAMPLES Example 1 Synthesis of dipyrrolo[1,2-b:1,2′-g][2,6]naphthyridine-5,11-dione (1a (A-1)) by the Condensation of 2-fromylpyrrole and succinyl chloride

Procedure 1.

2-Formylpyrrole (1.14 g, 12.0 mmol) and 4-dimethylaminopyridine (DMAP, 98 mg, 0.80 mmol) were dissolved in 25 ml of dry dichloromethane. The mixture was stirred under an argon atmosphere and triethylamine (2.2 ml, 15.8 mmol) was added. Then succinyl chloride (0.44 ml, 4.0 mmol) was added dropwise. The stirring was continued for 2 h at room temperature. Reaction mixture contained a large amount of a black tar, which was removed by filtration through Celite. Celite was then washed with dichloromethane. To the combined filtrates water was added and the layers were separated. Aqueous layer was extracted three times with dichloromethane. Combined organic layers were washed twice with water and dried over Na₂SO₄. The drying agent was filtered off and the solvents were evaporated. The product was purified by column chromatography (silica, dichloromethane:acetone 19:1) and recrystallized by slow addition of pentane to the solution of product in small amount of hot chloroform. Compound 1a (32 mg, 3.4% yield) was obtained as brown powder. Mp. >280° C. (decomposition). ¹H NMR (500 MHz, CDCl₃) δ 7.97 (s, 1H, CH (6-membered ring)), 7.81 (dd, J=3.1, 0.7 Hz, 1H, pyrrole: 5-H), 6.80 (dd, J=3.6, 1.2 Hz, 1H, pyrrole: 3-H), 6.54 (t, J=3.4 Hz, 1H, pyrrole: 4-H). ¹³C NMR (126 MHz, CDCl₃) δ 158.4, 131.7, 125.2, 123.6, 120.3, 118.4, 116.2. HRMS (EI) calcd for C₁₄H₈N₂O₂(M⁺): 236.0586; found: 236.0580. Elemental analysis calcd (%) for C₁₄H₈N₂O₂: C, 71.18, H, 3.41, N, 11.86; found: C, 71.19, H, 3.60, N, 11.65.

In addition to the dye 1a, unreacted 2-formylpyrrole (0.74 g, 65% of the initial amount) was also separated from the reaction mixture.

Procedure 2.

A mixture consisting of 2-formylpyrrole (238 mg, 2.5 mmol), powdered potassium carbonate (1.38 g, 10.0 mmol) and 10 ml of dry DMF was stirred under an argon atmosphere at 0° C. The solution of succinyl chloride (110 μl, 1.0 mmol) in 1.0 ml of dry dichloromethane was added dropwise. The stirring was continued for 2 h at 0° C. The reaction mixture was then diluted with water and passed through Celite, which was washed twice with water. Then two portions of ethanol and three portions of chloroform were passed through Celite in order to recover the product. These filtrates were combined and washed twice with water and dried over Na₂SO₄. The drying agent was filtered off and the solvents were evaporated. The product was recrystallized by slow addition of pentane to its solution in small amount of hot chloroform. Compound 1a (15 mg, 6.4% yield) was obtained as a brown powder. The product was identified by the comparison with previously synthesized sample.

Example 2 Synthesis of dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (1a (A-1)) by the Vilsmeier-Haack Formylation of 1,4-di(pyrrol-1-yl)butane-1,4-dione (3)

A mixture of succinamide (1.16 g, 10 mmol), 2,5-dimethoxytetrahydrofuran (3.9 ml, 30 mmol), para-toluenesulfonic acid monohydrate (190 mg, 1.0 mmol) and 25 ml of toluene was refluxed for 2 h under the Dean-Stark apparatus. The reaction mixture was cooled and the black precipitate, which was formed in the reaction, was filtered off and washed with chloroform. The filtrates were washed with water three times and dried over Na₂SO₄. Solvents were evaporated and the product was purified by the column chromatography (silica, hexanes:dichloromethane 1:2). The product was recrystallized from ethanol. Compound 3 (632 mg, 29% yield) was obtained as a white powder. Mp. 162-164° C. ¹H NMR (500 MHz, CDCl₃) δ 7.36 (br s, 4H, pyrrole: 2-H and 5-H), 6.36-6.27 (m, 4H, pyrrole: 3-H and 4-H), 3.34 (s, 4H, CH₂CH₂). ¹³C NMR (126 MHz, CDCl₃) δ 168.2, 119.0, 113.5, 28.9. HRMS (EI) calcd for C₁₂H₁₂N₂O₂ (M⁺): 216.0899; found: 216.0910. Elemental analysis calcd (%) for C₁₂H₁₂N₂O₂: C, 66.65, H, 5.59, N, 12.96; found: C, 66.86, H, 5.73, N, 12.92.

Under an argon atmosphere, to the solution of compound 3 (432 mg, 2.0 mmol) in 10 ml of dry 1,2-dichloroethane was added DMF (390 μl, 5.0 mmol). Then phosphorus(V) oxychloride (480 μl, 5.2 mmol) was added dropwise and the mixture was refluxed for 2 h. The reaction was quenched by the addition of saturated aqueous solution of sodium bicarbonate (10 ml). The resulting mixture was stirred for 5 min and diluted with dichloromethane and water. Layers were separated and the aqueous layer was extracted three times with dichloromethane. The combined organic layers were washed with water and dried over Na₂SO₄. The products were separated by column chromatography (silica, dichloromethane:acetone 19:1). Dye 1a was recrystallized by slow addition of pentane to its solution in small amount of hot chloroform. The product was obtained as a brown powder (39 mg, 8.3% yield) and identified by the comparison with previously synthesized sample. In addition to compound 1a, 2-formylpyrrole (127 mg, 33% yield) was also obtained.

Example 3 Acylation of Compound 3 (A-2) with Acetic Acid

Compound 3 (216 mg, 1.0 mmol) was dissolved in 4.5 ml of dry dichloromethane under an argon atmosphere, and the solution was cooled to 0° C. Trifluoroacetic anhydride (3.0 ml, 22 mmol) and acetic acid (460 μl, 8.0 mmol) were added and the resulting mixture was stirred at 0° C. for 10 min and then at room temperature for 4 h. The reaction mixture was then poured into a beaker containing 20 ml of saturated aqueous NaHCO₃ and mixed (CO₂ gas evolved). When the evolution of carbon dioxide was no longer observed, layers were separated. Aqueous layer was extracted three times with chloroform, and the combined organic layers were washed with water and dried over Na₂SO₄. Obtained mixture was separated using column chromatography (silica, hexanes:dichloromethane 1:2→pure dichloromethane) to give two crude products, compounds 4 and 1b, which were recrystallized by slow addition of methanol to a hot solution of the dye in small amount of chloroform.

6,12-Dimethyl-3-trifluoroacetyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (4)

Compound 4 (34 mg, 9.4% yield) was obtained as a dark brown powder. Mp. >180° C. (decomposition). ¹H NMR (500 MHz, CDCl₃) δ 7.84 (d, J=1.9 Hz, 1H, DPND: 9-H), 7.19 (d, J=3.9 Hz, 1H, DPND: 1-H), 6.97 (d, J=3.1 Hz, 1H, DPND: 7-H), 6.89 (d, J=4.0 Hz, 1H, DPND: 2-H), 6.56 (t, J=3.4 Hz, 1H, DPND: 8-H), 2.86 (s, 3H, CH₃), 2.81 (s, 3H, CH₃). ¹³C NMR (126 MHz, CDCl₃) δ 174.1-173.5 (m), 158.4, 143.3, 139.4, 137.8, 133.4, 128.4, 124.3, 124.3, 123.9, 119.1, 118.9, 116.0, 116.1 (q, J=290 Hz), 114.80, 114.54, 18.27, 17.81. HRMS (ESI) calcd for C₁₈H₁₁F₃N₂O₃Na (M+Na⁺): 383.0619; found: 383.0606. Elemental analysis calcd (%) for C₁₈H₁₁F₃N₂O₃: C, 60.01, H, 3.08, N, 7.78; found: C, 59.92, H, 3.02, N, 7.68.

6,12-Dimethyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (1b)

Compound 1b (33 mg, 12% yield) was obtained as a dark brown powder. Mp. >280° C. (decomposition). ¹H NMR (500 MHz, CDCl₃) δ 7.84 (d, J=1.7 Hz, 2H, pyrrole: 5-H), 6.95-6.85 (m, 2H, pyrrole: 3-H), 6.54 (t, J=3.3 Hz, 2H, pyrrole: 4-H), 2.85 (s, 6H, CH₃). ¹³C NMR (126 MHz, CDCl₃) δ 159.1, 140.5, 133.7, 122.7, 117.1, 115.6, 115.0, 18.3. HRMS (ESI) calcd for C₁₆H₁₂N₂O₂Na (M+Na⁺): 287.0796; found: 287.0786. Elemental analysis calcd (%) for C₁₆H₁₂N₂O₂: C, 72.72, H, 4.58, N, 10.60; found: C, 72.79, H, 4.50, N, 10.62.

Example 4 General Procedure for the Preparation of 6,12-Disubstituted DPND Derivatives (1b-1e)

Compound 3 (108 mg, 0.50 mmol) was dissolved in 3.0 ml of dry dichloromethane under an argon atmosphere, and the solution was cooled to 0° C. Subsequently, to the reaction flask were slowly added: carboxylic acid (3.0 mmol), trifluoroacetic anhydride (830 μl, 6.0 mmol) and trifluoroacetic acid (230 μl, 3.0 mmol). The resulting mixture was stirred at room temperature for given time. The reaction mixture was then slowly poured into a beaker containing 20 ml of vigorously stirred saturated aqueous NaHCO₃ (CO₂ evolved). When the evolution of carbon dioxide was no longer observed, the mixture was diluted with chloroform and layers were separated. Aqueous layer was extracted four times with chloroform, and the combined organic layers were washed with water and dried over Na₂SO₄. The product was purified by column chromatography and recrystallized (see below for details).

6,12-Dimethyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (1b (A-2))

Carboxylic acid used: acetic acid (172 μl, 3.0 mmol). Reaction time: 5 h. Product was purified using column chromatography (silica, dichloromethane) and recrystallized by slow addition of methanol to a hot solution of the dye in small amount of chloroform. Compound 1b (23 mg, 17% yield) was obtained as a dark brown powder and identified by the comparison with previously synthesized sample.

6,12-Diheptyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (1c (A-3))

Carboxylic acid used: caprylic acid (475 μl, 3.0 mmol). Reaction time: 3 h. Product was purified using column chromatography (silica, hexanes:dichloromethane 2:1→1:1) and recrystallized by slow addition of methanol to a solution of the dye in small amount of dichloromethane. Compound 1c (63 mg, 29% yield) was obtained as a red solid. Mp. 107-109° C. ¹H NMR (500 MHz, CDCl₃) δ 7.84 (dd, J=3.0, 1.3 Hz, 2H, pyrrole: 5-H), 6.87 (dd, J=3.7, 1.3 Hz, 2H, pyrrole: 3-H), 6.54 (t, J=3.4 Hz, 2H, pyrrole: 4-H), 3.35-3.22 (m, 4H, CH₂(CH₂)₅CH₃), 1.76-1.62 (m, 4H, CH₂(CH₂)₅CH₃), 1.58-1.47 (m, 4H, CH₂(CH₂)₅CH₃), 1.44-1.35 (m, 4H, CH₂(CH₂)₅CH₃), 1.35-1.23 (m, 8H, CH₂(CH₂)₅CH₃), 0.89 (t, J=6.9 Hz, 6H, CH₂(CH₂)₅CH₃). ¹³C NMR (126 MHz, CDCl₃) δ 158.6, 145.6, 133.4, 122.6, 116.7, 115.6, 114.6, 32.1, 31.2, 30.6, 30.5, 29.4, 22.8, 14.3. HRMS (ESI) calcd for C₂₈H₃₇N₂O₂ (M+H⁺): 433.2855; found: 433.2848. Elemental analysis calcd (%) for C₂₈H₃₆N₂O₂: C, 77.74, H, 8.39, N, 6.48; found: C, 77.48, H, 8.48, N, 6.33.

The synthesis of compound 1c was repeated in 10-times larger scale, using the same procedure and following amounts of reagents: compound 3 (1.08 g, 5.00 mmol), caprylic acid (4.75 ml, 30 mmol), trifluoroacetic anhydride (8.3 ml, 60 mmol), trifluoroacetic acid (2.30 ml, 30 mmol) and dichloromethane (30 ml) as a solvent. After 3.5 h of the reaction at room temperature 525 mg of product 1c was obtained (23% yield).

6,12-Di-sec-butyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (1d (A-4))

Carboxylic acid used: 2-methylbutyric acid (330 μl, 3.0 mmol). Reaction time: 6 h. Product was purified using column chromatography (silica, hexanes:dichloromethane 1:1) and recrystallized by slow addition of methanol to a solution of the dye in small amount of dichloromethane. Compound 1d (36 mg, 21% yield) was obtained as red crystals. Mp. 176-178° C. ¹H NMR (500 MHz, CDCl₃) δ 7.79 (dd, J=2.9, 1.0 Hz, 2H, pyrrole: 5-H), 7.01 (d, J=3.0 Hz, 2H, pyrrole: 3-H), 6.50 (t, J=3.4 Hz, 2H, pyrrole: 4-H), 4.74 (br s, 2H, C—(CH₃)CH₂CH₃), 2.00-1.90 (m, 2H, CH(CH₃)CH₂CH₃), 1.90-1.79 (m, 2H, CH(CH₃)CH₂CH₃), 1.46 (dd, J=7.1, 1.7 Hz, 6H, CH(CH₃)CH₂CH₃), 0.96 (t, J=7.4 Hz, 6H, CH(CH₃)CH₂CH₃). ¹³C NMR (126 MHz, CDCl₃) δ 159.7, 150.7, 130.3, 121.6, 118.7, 116.8, 115.2, 35.9, 30.6, 20.5, 13.1. HRMS (ESI) calcd for C₂₂H₂₄N₂O₂Na (M+Na⁺): 371.1735; found: 371.1724. Elemental analysis calcd (%) for C₂₂H₂₄N₂O₂: C, 75.83, H, 6.94, N, 8.04; found: C, 75.63, H, 6.89, N, 7.94.

6,12-Bis(4-methoxybenzyl)dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (1e (A-5))

Carboxylic acid used: 4-methoxyphenylacetic acid (499 mg, 3.0 mmol). Reaction time: 6 h. Product was purified using column chromatography (silica, dichloromethane→dichloromethane:ethyl acetate 19:1) and recrystallized by slow addition of methanol to a solution of the dye in small amount of chloroform. Compound 1e (25 mg, 10.5% yield) was obtained as red crystals. Mp. >270° C. (decomposition). ¹H NMR (500 MHz, CDCl₃) δ 7.82 (dd, J=3.0, 1.2 Hz, 2H, pyrrole: 5-H), 7.24-7.18 (AA′BB′, 4H, benzene: 2-H and 6-H), 6.91 (dd, J=3.7, 1.2 Hz, 2H, pyrrole: 3-H), 6.83-6.78 (AA′BB′, 4H, benzene: 3-H and 5-H), 6.52 (t, J=3.4 Hz, 2H, pyrrole: 4-H), 4.69 (s, 4H, CH₂Ar), 3.75 (s, 6H, OCH₃). ¹³C NMR (126 MHz, CDCl₃) δ 158.2, 158.0, 142.4, 133.6, 130.8, 129.3, 123.1, 118.2, 115.8, 115.3, 113.9, 55.2, 34.7. HRMS (ESI) calcd for C₃₀H₂₄N₂O₄Na (M+Na⁺): 499.1634; found: 499.1624. Elemental analysis calcd (%) for C₃₀H₂₄N₂O₄: C, 75.62, H, 5.08, N, 5.88 found: C, 75.65, H, 5.10, N, 5.92.

6,12-Diethyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (1f (A-6))

Compound 3 (216 mg, 1.0 mmol) was dissolved in 6.0 ml of dry dichloromethane under an argon atmosphere, and the solution was cooled to 0° C. Subsequently, to the reaction flask were slowly added: propionic anhydride (380 μl, 3.0 mmol), trifluoroacetic anhydride (1.10 ml, 7.9 mmol) and trifluoroacetic acid (920 μl, 12.0 mmol). The resulting mixture was stirred at room temperature for 2 h. The reaction mixture was then slowly poured into a beaker containing 20 ml of vigorously stirred saturated aqueous NaHCO₃ (CO₂ evolved). When the evolution of carbon dioxide was no longer observed, the mixture was diluted with chloroform and layers were separated. Aqueous layer was extracted four times with chloroform, and the combined organic layers were washed with water and dried over Na₂SO₄. The product was purified by column chromatography (silica, toluene) and recrystallized by slow addition of methanol to the solution of product in small amount of dichloromethane. Compound 1f (67 mg, 23%) was obtained as dark red crystals. Mp. 226-229° C. ¹H NMR (500 MHz, CDCl₃) δ 7.84 (dd, J=3.0, 1.3 Hz, 2H, pyrrole: 5-H), 6.89 (dd, J=3.6, 1.3 Hz, 2H, pyrrole: 3-H), 6.55 (t, J=3.4 Hz, 2H, pyrrole: 4-H), 3.33 (q, J=7.4 Hz, 4H, CH₂CH₃), 1.35 (t, J=7.4 Hz, 6H, CH₂OCH₃). ¹³C NMR (126 MHz, CDCl₃) δ 158.5, 146.8, 133.0, 122.7, 116.7, 115.7, 114.5, 24.4, 14.5. HRMS (ESI) calcd for C₁₈H₁₆N₂O₄Na (M+Na⁺): 315.1109; found: 315.1097.

Synthesis of Various 6,12-Disubstituted DPND Derivatives.^([a])

Carboxylic acid Reaction time Product T¹ Yield CH₃CO₂H 5 h 1b (A-2) CH₃   17% C₇H₁₅CO₂H 3 h^([c]) 1c (A-3) C₇H₁₅   29%^([c]) 3.5 h^([d])   23%^([d])

6 h Id (A-4) sec-butyl   21%

6 h le (A-5) 4-methoxybenzyl 10.5% (C₂H₅CO)₂O ^([b]) 2 h 1f (A-6) C₂H₅   23% [a] Reagents proportions: 3 (0.5 mmol), carboxylic acid (3 mmol), TFAA (6 mmol), TFA (3 mmol). ^([b]) Propionic anhydride used instead of carboxylic acid. ^([c])0.5 mmol scale. ^([d])5.0 mmol scale.

Example 4 3,9-Dibromo-6,12-diheptyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (5 (C-1))

A solution of compound 1c (108 mg, 0.25 mmol) in 5 ml of chloroform was stirred at 0° C. (water-ice bath). Freshly recrystallized N-bromosuccinimide (93 mg, 0.52 mmol) was added and the obtained mixture was stirred in the darkness (protection with aluminium foil) for 16 h. During this time ice in the ice bath melted and the reaction mixture warmed to the room temperature. The reaction mixture was diluted with chloroform, washed with water three times, and dried over Na₂SO₄. The product was purified using column chromatography (silica, hexanes:dichloromethane 3:1→2:1) and recrystallized by slow addition of methanol to a solution of the dye in small amount of dichloromethane. Compound 5 (107 mg, 72% yield) was obtained as a red solid. Mp. 133-135° C. ¹H NMR (500 MHz, CDCl₃) δ 6.81 (d, J=4.0 Hz, 2H, pyrrole: 3-H), 6.59 (d, J=4.0 Hz, 2H, pyrrole: 4-H), 3.24-3.05 (m, 4H, CH₂(CH₂)₅CH₃), 1.71-1.59 (m, 4H, CH₂(CH₂)₅CH₃), 1.55-1.46 (m, 4H, CH₂(CH₂)₅CH₃), 1.41-1.23 (m, 12H, CH₂(CH₂)₅CH₃), 0.89 (t, J=6.8 Hz, 6H, CH₂(CH₂)₅CH₃). ¹³C NMR (126 MHz, CDCl₃) δ 158.9, 143.3, 135.0, 120.5, 115.8, 115.4, 106.6, 31.9, 30.3, 30.2 (2 signals), 29.2, 22.7, 14.1. HRMS (ESI) calcd for C₂₈H₃₄Br₂N₂O₂ (M⁺): 588.0987; found: 588.0985. Elemental analysis calcd (%) for C₂₈H₃₄Br₂N₂O₂: C, 56.96, H, 5.80, N, 4.74; found: C, 56.98, H, 5.77, N, 4.76.

The synthesis of compound 5 was repeated in 4-times larger scale, using the same procedure and following amounts of reagents: compound 1c (433 mg, 1.00 mmol), N-bromosuccinimide (374 mg, 2.10 mmol) and chloroform (15 ml) as a solvent. 379 mg of the product 5 was obtained (64% yield).

Example 5 3,9-Dicyano-6,12-diheptyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (6 (A-7))

A mixture of compound 5 (59 mg, 0.10 mmol), copper(I) cyanide (20 mg, 0.22 mmol) and 2 ml of dry NMP was stirred under argon at 140° C. for 16 h and at 160° C. for 5 h. The mixture was diluted with water and passed through Celite, which was washed with water. Then the product was extracted from Celite with one portion of ethanol and three portions of chloroform. The organic filtrates were combined, washed with water twice and dried over Na₂SO₄. Product was purified by column chromatography (silica, hexanes:dichloromethane 2:3). After evaporation of eluent 16 mg of product was obtained (33% yield), which was recrystallized by slow addition of methanol to warm solution of the dye in small amount of chloroform. Compound 6 (11 mg, 23% yield) was obtained as red crystals. Mp. 222-225° C. ¹H NMR (500 MHz, CDCl₃) δ 7.19 (d, J=4.0 Hz, 2H, pyrrole: 3-H), 6.92 (d, J=4.0 Hz, 2H, pyrrole: 4-H), 3.43-3.15 (m, 4H, CH₂(CH₂)₅CH₃), 1.76-1.62 (m, 4H, CH₂(CH₂)₅CH₃), 1.59-1.47 (m, 4H, CH₂(CH₂)₅CH₃), 1.42-1.25 (m, 12H, CH₂(CH₂)₅CH₃), 0.90 (t, J=6.8 Hz, 6H, CH₂(CH₂)₅CH₃). ¹³C NMR (126 MHz, CDCl₃) δ 156.8, 146.6, 136.2, 127.0, 116.9, 116.0, 112.5, 106.4, 31.8, 31.1, 30.2, 30.1, 29.1, 22.7, 14.1. HRMS (ESI) calcd for C₃₀H₃₄N₄O₂Na (M+Na⁺): 505.2579; found: 505.2574.

Example 6 General Procedure for the Sonogashira Coupling of Compound 5 (C-1) with Para-Substituted Phenylacetylenes—Synthesis of Compounds 7a-d

In a Schlenck flask containing a magnetic stirring bar were placed: bromoderivative 5 (0.10 mmol, 59 mg), copper(I) iodide (1.9 mg, 0.010 mmol), tetrakis(triphenylphosphine)palladium(0) (5.8 mg, 0.005 mmol), and para-substituted phenylacetylene (0.30 mmol). The vessel was evacuated and backfilled with argon (3 times) and anhydrous, degassed THF was added (3 ml) followed by dry triethylamine (56 μl, 0.40 mmol). The vessel was tightly closed and again carefully evacuated (until the mixture start to boil) and backfilled with argon (3 times). The content of the flask was stirred for 20 h at 70° C. (above the boiling point). Solvents were evaporated and the product was purified as described below.

6,12-Diheptyl-3,9-bis((4-nitrophenyl)ethynyl)dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (7a (A-8))

Prepared from 4-nitrophenylacetylene (44 mg, 0.30 mmol). Product was purified using column chromatography (silica, hexanes:dichloromethane 1:1→1:2) and recrystallized from toluene. Compound 7a (56 mg, 78% yield) was obtained as a dark violet powder. Mp. >400° C. ¹H NMR (500 MHz, CDCl₃, 50° C.) δ 8.26-8.18 (AA′BB′, 4H, benzene: 3-H and 5-H), 7.77-7.67 (AA′BB′, 4H, benzene: 2-H and 6-H), 6.89 (s, 4H, pyrrole: 3-H and 4-H), 3.34-3.27 (m, 4H, CH₂(CH₂)₅CH₃), 1.80-1.69 (m, 4H, CH₂(CH₂)₅CH₃), 1.61-1.54 (m, 4H, CH₂(CH₂)₅CH₃), 1.44-1.23 (m, 12H, CH₂(CH₂)₅CH₃), 0.90 (t, J=6.9 Hz, 6H, CH₂(CH₂)₅CH₃). ¹³C NMR (126 MHz, CDCl₃, 50° C.) δ 158.4, 147.5, 144.3, 135.5, 132.2, 130.3, 123.8, 118.6, 116.9, 116.3, 96.2, 88.1, 32.1, 31.0, 30.5 (2 signals), 29.2, 22.8, 14.2. Elemental analysis calcd (%) for C₄₄H₄₂N₄O₆: C, 73.11, H, 5.86, N, 7.75; found: C, 73.20, H, 5.93, N, 7.71.

6,12-Diheptyl-3,9-bis((4-(trifluoromethyl)phenyl)ethynyl)dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (7b (A-9))

Prepared from 4-(trifluoromethyl)phenylacetylene (51 mg, 0.30 mmol). Product was purified using column chromatography (silica, hexanes:dichloromethane 4:1→3:7) and recrystallized by slow addition of methanol to hot solution of the dye in small amount of chloroform. Compound 7b (44 mg, 57% yield) was obtained as a dark green powder. Mp. 200-203° C. ¹H NMR (500 MHz, CDCl₃) δ 7.76-7.67 (AA′BB′, 4H, benzene: 3-H and 5-H), 7.67-7.58 (AA′BB′, 4H, benzene: 2-H and 6-H), 6.89 (d, J=4.0 Hz, 2H, pyrrole: 3-H), 6.87 (d, J=4.0 Hz, 2H, pyrrole: 4-H), 3.34-3.23 (m, 4H, CH₂(CH₂)₅CH₃), 1.77-1.68 (m, 4H, CH₂(CH₂)₅CH₃), 1.59-1.52 (m, 4H, CH₂(CH₂)₅CH₃), 1.48-1.40 (m, 4H, CH₂(CH₂)₅CH₃), 1.38-1.29 (m, 8H, CH₂(CH₂)₅CH₃), 0.89 (t, J=7.0 Hz, 6H, CH₂(CH₂)₅CH₃). ¹³C NMR (126 MHz, CDCl₃) δ 158.5, 144.0, 135.1, 131.8, 125.5, 125.4, 123.4, 118.8, 116.6, 116.1, 96.5, 85.2, 32.1, 30.9, 30.5, 29.9, 29.2, 22.8, 14.3 (signals of CF₃ group and adjacent carbon atom were not identified due to low intensities caused by ¹³C-¹⁹F coupling). HRMS (ESI) calcd for C₄₆H₄₂F₆N₂O₂(M⁺): 768.3150; found: 768.3153.

6,12-Diheptyl-3,9-bis((4-methoxyphenyl)ethynyl)dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (7c (A-10))

Prepared from 4-methoxyphenylacetylene (40 mg, 0.30 mmol). Product was purified using column chromatography (silica, hexanes:dichloromethane 3:2→5:4) and recrystallized by slow addition of methanol to solution of the dye in small amount of dichloromethane. Compound 7c (33 mg, 48% yield) was obtained as a dark violet powder. Mp. 185-187° C. ¹H NMR (500 MHz, CDCl₃) δ 7.64-7.48 (AA′BB′, 4H, benzene: 2-H and 6-H), 6.95-6.87 (AA′BB′, 4H, benzene: 3-H and 5-H), 6.84 (d, J=4.0 Hz, 2H, pyrrole: 3-H), 6.77 (d, J=3.9 Hz, 2H, pyrrole: 4-H), 3.85 (s, 6H, OCH₃), 3.34-3.21 (m, 4H, CH₂(CH₂)₅CH₃), 1.78-1.66 (m, 4H, CH₂(CH₂)₅CH₃), 1.60-1.51 (m, 4H, CH₂(CH₂)₅CH₃), 1.48-1.39 (m, 4H, CH₂(CH₂)₅CH₃), 1.39-1.27 (m, 8H, CH₂(CH₂)₅CH₃), 0.90 (t, J=6.5 Hz, 6H, CH₂(CH₂)₅CH₃). ¹³C NMR (126 MHz, CDCl₃) δ 160.0, 158.6, 143.3, 134.3, 133.2, 122.1, 119.7, 116.0, 115.8, 115.5, 114.1, 98.3, 81.9, 55.3, 32.0, 30.7, 30.3, 29.0, 22.7, 14.2. HRMS (ESI) calcd for C₄₆H₄₈N₂O₄Na (M+Na⁺): 715.3512; found: 715.3506.

3,9-Bis((4-(dimethylamino)phenyl)ethynyl)-6,12-diheptyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (7d (A-11))

Prepared from 4-(dimethylamino)phenylacetylene (44 mg, 0.30 mmol). Product was purified using column chromatography (silica, hexanes:dichloromethane 1:1→1:3) and recrystallized by slow addition of methanol to solution of the dye in small amount of dichloromethane. Compound 7d (40 mg, 56% yield) was obtained as a black powder. Mp. 235-239° C. ¹H NMR (500 MHz, CDCl₃) δ 7.57-7.46 (AA′BB′, 4H, benzene: 2-H and 6-H), 6.83 (d, J=4.0 Hz, 2H, pyrrole: 3-H), 6.74 (d, J=4.0 Hz, 2H, pyrrole: 4-H), 6.73-6.59 (m, 4H, benzene: 3-H and 5-H), 3.32-3.23 (m, 4H, CH₂(CH₂)₅CH₃), 3.02 (s, 12H, NCH₃), 1.77-1.68 (m, 4H, CH₂(CH₂)₅CH₃), 1.59-1.52 (m, 4H, CH₂(CH₂)₅CH₃), 1.47-1.40 (m, 4H, CH₂(CH₂)₅CH₃), 1.37-1.30 (m, 8H, CH₂(CH₂)₅CH₃), 0.90 (t, J=6.8 Hz, 6H, CH₂(CH₂)₅CH). ¹³C NMR (126 MHz, CDCl₃) δ 158.7, 150.2, 142.8, 134.0, 132.9, 121.5, 120.2, 115.8, 111.9, 99.9, 81.8, 40.3, 32.1, 30.7, 30.4, 29.1, 22.7, 14.2. HRMS (ESI) calcd for C₄₈H₅₅N₄O₂ (M+H⁺): 719.4325; found: 719.4325. Elemental analysis calcd (%) for C₄₈H₅₄N₄O₂: C, 80.19, H, 7.57, N, 7.79; found: C, 80.08, H, 7.50, N, 7.72.

Example 7 Synthesis of 1,4-di(pyrrol-1-yl)butane-1,4-dione (3), Modified Procedure

To a solution of pyrrole (0.54 mL, 7.74 mmol) in THF (20 mL) was added n-butyllithium (2.94 mL, 2.7 M in hexane, 7.94 mmol) at −40° C. After stirring for 15 min at 0° C. the solution was again cooled to −40° C. and succinylchloride (0.43 mL, 3.91 mmol) was added dropwise. The reaction mixture was stirred at room temperature for 3 h, quenched with water (10 mL) and then poured onto water (150 mL). The product precipitated as a beige powder and was used in the next step without further purification.

Synthesis of 6,12-Dinonyldipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (1g (A-16))

Compound 1g was made according to the general procedure given for compounds 1a-1e: compound 3 (3.00 g, 14 mmol), decanoic acid (14.34 g, 83.0 mmol), trifluoroacetic anhydride (34.97 g, 166 mmol), trifluoroacetic acid (9.49 g, 83 mmol), methylenechloride 90 ml. Reaction time: 15 h. Product was purified using column chromatography over silica gel. Compound 1g was obtained as a red solid. ¹H NMR (300 MHz, CDCl₃) δ 7.84 (dd, 2H), 6.88 (dd, 2H), 6.54 (t, 2H), 3.35-3.25 (m, 4H), 1.71-1.61 (m, 4H), 1.58-1.45 (m, 4H), 1.42-1.12 (m, 20H), 0.93-0.80 (t, 6H).

Example 8 Synthesis of Compound (1h (A-17))

Compound 1h was made according to the general procedure given for compounds 1a-1e from compound 3, 4-octyl-tetradecanoic acid [1448593-51-8], trifluoroacetic anhydride, trifluoroacetic acid. Reaction time: 15 h. Product was purified using column chromatography over silica gel.

Example 9 Synthesis of Compound (1i (A-18))

Compound 1i was made according to the general procedure given for compounds 1a-1e from compound 3, dodecanoic acid, trifluoroacetic anhydride, trifluoroacetic acid. Reaction time: 15 h. Product was purified using column chromatography over silica gel.

Example 10 Synthesis of Compound (5a (C-6))

Compound 5a was made according to the general procedure given for compounds 5 from compound 1i, and NBS. Product was purified using column chromatography over silica gel.

Example 11 General Procedure for the Synthesis of Compounds 8a and 8b

In a Schlenck flask containing a magnetic stirring bar were placed: compound 5a (C-6) (0.1 mmol, 72.6 mg, 1.0 eq), palladium(II) acetate (2.2 mg, 0.01 mmol, 10 mol %), tri(o-tolyl)phosphine (6.1 mg, 0.02 mmol, 20 mol %). The vessel was evacuated and backfilled with argon (3 times) and anhydrous, degassed DMF was added (6 ml) followed by argonated (i-Pr)₂NEt (Hünig's base) (0.1 mL) and styrene (0.4 mmol, 4.0 eq). The vessel was tightly closed and again carefully evacuated and backfilled with argon (3 times). The content of the flask was stirred at 90° C. for 24 h. All volatiles were evaporated and the product was purified as described below.

3,9-Bis((E)-4-cyanostyryl)-6,12-diundecyl-5H,11H-dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (8a (A-19))

Prepared from 4-cynanostyrene (51.7 mg, 0.4 mmol). Product was purified using column chromatography (SiO₂, cyclohexane:dichloromethane 1:1 then 1:2) and recrystallized by slow addition of methanol to hot solution of the dye in small amount of chloroform. Compound 8a (44.7 mg, 56% yield) was obtained as a dark brown crystals. ¹H NMR (500 MHz, CDCl₃) δ 8.50 (d, 2H, J=13.2 Hz), 7.63 (m, 8H), 7.06 (d, 2H, J=16.4 Hz), 6.95 (d, 2H, J=4.0 Hz), 6.91 (d, 2H, J=4.1 Hz), 3.25 (t, 4H, J=7.7 Hz), 1.69 (m, 4H), 1.56 (m, 4H+H₂O in CDCl₃), 1.41 (m, 4H,) 1.30 (m, 24H+solvents residues), 0.88 (t, 6H, J=6.5 Hz). ¹³C NMR (125 MHz, CDCl₃) δ 160.7, 143.3, 141.7, 138.9, 135.5, 132.5, 128.9, 127.1, 123.4, 119.0, 116.7, 115.8, 114.9, 110.7, 31.9, 30.7, 30.5, 30.3, 29.7, 29.7, 29.5, 29.4, 22.7, 14.1. HRMS (EI) calcd for C₅₄H₆₂N₄O₂ 798.4873 [M′⁺], found 798.4851.

3,9-Bis((E)-3-methoxystyryl)-6,12-diundecyl-5H,11H-dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (8b (A-20))

Prepared from 3-methoxystyrene (53.7 mg, 0.4 mmol, 55.5 μL). Product was purified using column chromatography (SiO₂, cyclohexane:dichloromethane 3:2). The obtained fraction was washed with methanol until the washings were colorless to give sufficiently pure compound. Compound 8b (41.3 mg, 51% yield) was obtained as a dark brown crystals.

¹H NMR (500 MHz, CD₂Cl₂) δ 8.35 (d, 2H, J=13.2 Hz), 7.30 (t, 2H, J=6.0 Hz), 7.17 (d, 2H, J=6.0 Hz), 7.08 (t, 4H, J=8.7 Hz), 6.92 (m, 4H), 7.08 (d, 2H, J=6.4 Hz), 3.80 (s, 6H), 3.26 (t, 4H, J=6.0 Hz), 1.70 (m, 4H), 1.55 (m, 4H), 1.40 (m, 4H,) 1.28 (m, 24H+solvents residues), 0.88 (t, 6H, J=5.6 Hz). ¹³C NMR (125 MHz, CD₂Cl₂) δ 171.9, 161.3, 160.5, 143.1, 140.0, 139.2, 135.4, 131.2, 130.0, 120.8, 119.7, 116.8, 115.9, 114.3, 113.9, 112.5, 55.6, 32.3, 31.0, 30.9, 30.7, 30.1, 30.1, 29.9, 29.8, 23.1, 14.3. HRMS (EI) calcd for C₅₄H₆₈N₂O₄ 808.5179 [M′⁺], found 808.5165.

Example 12 General Procedure for the Direct Coupling of DPND and Bromoarenes

In a Schlenk flask containing a magnetic stirring bar were placed: compound 1c (A-3) (0.1 mmol, 43.3 mg, 1.0 eq), palladium(II) acetate (1.1 mg, 0.005 mmol, 5 mol %), PCy₃.HBF₄ (3.7 mg, 0.01 mmol, 10 mol %), pivalic acid (3.1 mg, 0.03 mmol, 30% mol), K₂CO₃ (55.2 mg, 0.4 mmol, 4.0 eq) and, if a solid, the bromoarene (0.25 mmol, 2.5 eq). The vessel was evacuated and backfilled with argon (3 times). If the bromoarene (0.25 mmol, 2.5 eq) was a liquid, it was added next using a syringe followed by anhydrous, degassed toluene (3 mL). The vessel was tightly closed and again carefully evacuated and backfilled with argon (3 times). The content of the flask was stirred at 120° C. for typically 24-72 h. After indicated time the flask was cooled down to room temperature and extracted three times with dichloromethane (3×25 mL), then dried over magnesium sulphate. All solvents were evaporated off and the residue was purified by column chromatography.

4,4′-(6,12-diheptyl-5,11-dioxo-5H,11H-dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-3,9-diyl)dibenzonitrile (9a (A-21))

Prepared using 4-bromocyanobenzene (45.5 mg, 0.25 mmol). Product was purified using column chromatography (SiO₂, n-hexane:dichloromethane 1:3) and recrystallized by slow addition of methanol to hot solution of the dye in small amount of chloroform. Compound (47.8 mg, 64% yield) was obtained as a dark brown crystals. R_(f)=0.42 (SiO₂, n-hexane/DCM, 1:3). ¹H NMR (500 MHz, CDCl₃) δ 7.68 (d, 4H, J=8.5 Hz), 7.56 (d, 4H, J=8.5 Hz), 6.92 (d, 2H, J=3.5 Hz), 6.59 (d, 2H, J=4.0 Hz), 3.20-3.17 (m, 4H), 1.71-1.67 (m, 4H), 1.50-1.44 (m, 4H,) 1.37-1.29 (m, 12H), 0.88 (t, 6H, J=6.5 Hz). ¹³C NMR (125 MHz, CDCl₃) δ 159.4, 144.2, 137.9, 137.3, 136.0, 131.4, 129.2, 119.5, 118.9, 116.0, 115.9, 111.2, 31.8, 30.5, 30.4, 30.1, 29.1, 22.7, 14.1. HRMS (ESI) calcd for C₄₂H₄₃N₄O₂ 635.3386 [M+H⁺], found 635.3383.

6,12-diheptyl-3,9-bis(4-nitrophenyl)-5H,11H-dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (9b (A-22))

Prepared using 4-bromonitrobenzene (43.3 mg, 0.25 mmol). Product was purified using column chromatography (SiO₂, cyclohexane:dichloromethane 1:1) and recrystallized from toluene. Compound (42.2 mg, 62% yield) was obtained as a dark brown crystals. R_(f)=0.30 (SiO₂, cyclohexane/DCM, 1:1). ¹H NMR (500 MHz, CDCl₃) δ 8.26 (d, 4H, J=8.5 Hz), 7.62 (d, 4H, J=7.2 Hz), 6.94 (d, 2H, J=4.0 Hz), 6.64 (d, 2H, J=3.5 Hz), 3.22-3.20 (m, 4H), 1.68-1.62 (m, 4H), 1.50-1.44 (m, 4H,) 1.37-1.25 (m, 12H), 0.87 (t, 6H, J=6.5 Hz). ¹³C NMR (125 MHz, CDCl₃) δ 159.3, 147.0, 144.4, 139.2, 137.5, 136.2, 129.3, 123.0, 119.8, 116.1, 116.1, 31.8, 30.6, 30.4, 30.1, 29.1, 22.7, 14.1.

6,12-diheptyl-3,9-bis(4-(methoxymethyl)phenyl)-5H, 11H-dipyrrolo[1,2-b:1′,2′-g][2,6]naphthyridine-5,11-dione (9c (A-23))

Prepared from 1-bromo-4-(methoxymethyl)benzene (43.3 mg, 0.25 mmol, 36.0 μL). Product was purified using two column chromatographies (SiO₂, dichloromethane). Compound (14.8 mg, 22% yield) was obtained as a dark brown crystals with copper luster. R_(f)=0.32 (SiO₂, DCM, 1:1). ¹H NMR (500 MHz, CDCl₃) δ 7.47 (d, 4H, J=8.0 Hz), 7.36 (d, 4H, J=8.0 Hz), 6.85 (d, 2H, J=3.5 Hz), 6.50 (d, 2H, J=3.5 Hz), 4.52 (s, 4H), 3.45 (s, 6H), 3.21-3.18 (m, 4H), 1.69-1.63 (m, 4H), 1.49-1.43 (m, 4H) 1.37-1.25 (m, 12H), 0.88 (t, 6H, J=6.5 Hz). ¹³C NMR (125 MHz, CDCl₃) δ 159.7, 143.3, 139.8, 137.9, 135.3, 132.3, 128.7, 126.9, 118.2, 115.8, 115.5, 74.5, 58.3, 31.8, 30.5, 30.2, 29.7, 29.2, 22.7, 14.1. HRMS (ESI) calcd for C₄₄H₅₃N₂O₄ 673.4005 [M+H⁺], found 673.3992.

Example 13 Synthesis of Polymer (P-9)

Compound A-16 (100.0 mg, 0.205 mmol), DPP [1224430-28-7] (231.5 mg, 0.205 mmol), pivalic acid (20.1 mg, 0.205 mmol), K₂CO₃ (113.1 mg, 0.818 mmol), Pd(OAc)₂ (2.3 mg, 0.01 mmol, 5 mol %) and PCy₃.HBF₄ (7.5 mg, 0.02 mol, 10 mol %) were placed in a Schlenk flask. The vessel was evacuated and backfilled with nitrogen (3 times), and anhydrous, degassed toluene was added via syringe. The Schlenk flask was closed and stirred at 120° C. for 48 h. The reaction mixture was cooled down to room temperature and poured into MeOH (150 mL). After filtration, the obtained solid was subjected to Soxhlet extraction (successively with heptane and toluene). Removing the solvent from the toluene fraction gave a bluish polymer. HT-GPC of the crude polymer: M_(n)=29,446 Da; M_(w)=77,720 Da; PD=2.64. The UV-Vis spectra of the polymer was recorded in toluene, which showed a strong absorption in the NIR with λ_(max) at 866 nm.

Example 14 Synthesis of Polymer (P-10)

Polymer P10 was made according to the procedure given for polymer P9 from compound A-16 and DPP [1801150-23-1]. M_(n)=19,717 Da; M_(w)=58,259 Da; PD=2.96.

Example 15 Synthesis of Polymer (P-11)

Polymer P11 was made according to the procedure given for polymer P9 from compound A-16 and compound 10. Mn=7,265 Da; M_(w)=15,068 Da; PD=2.07.

Example 16 Synthesis of Polymer (P-12)

Polymer P12 was made according to the procedure given for polymer P9 from compound A-16 and compound 11. M_(n)=8,577 Da; M_(w)=21,864 Da; PD=2.55.

Application Example A1 Fabrication and Electrical Characterization of an Organic Field-Effect Transistor (OFET) Based on Polymer P9

Preparation of Back-Contact, Top-Gate FETs

The compound is dissolved at a concentration of 0.75 wt % in chlorobenzene and subsequently spincoated (1200 rpm, 15 s) onto a PET-substrate with lithographically prepatterned gold contacts, serving as Source and Drain contact of the FET. After the coating is completed, the respective substrate is immediately transferred onto a preheated hotplate and heated for 30 s at 90° C. Next the gate dielectric layer consisting of Cytop CTL-809 M is spincoated on top of the organic semiconductor (1200 rpm, 30 s). After pincoating, the substrate is again transferred to the hotplate and annealed for another 30 Min at 90° C. The thickness of the dielectric layer is 620 nm measured by profilometer. Finally 70 nm thick shadow-mask patterned silver gate electrodes are deposited by vacuum evaporation to complete FETs in the BCTG-configuration.

Electrical Characterization

The mobility μ is calculated from the root representation of the transfer characteristic curve (solid grey curve) in the saturation region. The slope m is determined from the dashed black line in the FIGURE. The dashed black line in the FIGURE is fitted to a region of the square root representation of the Drain current ID such that a good correlation to the linear slope of the root representation is obtained.

The threshold voltage U_(Th) can be taken from the intersection of black dashed line in the FIGURE with the X-axis portion (V_(GS)).

In order to calculate the electrical properties of the OFET, the following equations are employed:

$\begin{matrix} {\mu = \frac{m^{2}*2\; L}{C_{G}*W}} \end{matrix}\mspace{14mu}\begin{matrix} {C_{G} = {ɛ_{0}*ɛ_{r}\frac{1}{d}}} \end{matrix}\mspace{14mu}\begin{matrix} {U_{Th} = {{- 1}*\frac{m}{d}}} \end{matrix}$ $\begin{matrix} {\frac{ON}{OFF} = \frac{I_{D}\max}{I_{D}\min}} \end{matrix}$ where ε₀ is the vacuum permittivity of 8.85×10⁻¹² As/Vm. ε_(r)=2.1 for Cytop and d is the thickness of the dielectric. The width over length ratio W/L is 25.

The following mobilities, threshold voltage and ON/OFF Ratio have been calculated for the respective polymer from an average of 27 TFTs:

Field-effect mobility Threshold voltage Compound μ [cm²/Vs] U_(TH) [V] ON/OFF ratio P9 0.013 −7.5 2E4 

The invention claimed is:
 1. A compound of formula R¹⁰—Ar—Y—Ar′—R¹⁰′  (I), wherein Ar is a group of formula —[Ar³]_(c)—[Ar²]_(b)—[Ar¹]_(a)—**, Ar′ is a group of formula **—[Ar^(1′)]_(a′)—[Ar^(2′)]_(b′)—[Ar^(3′)]_(c′)—, Y is a group of formula

wherein ** indicates the bonding to Y, a is 0, 1, 2, or 3, a′ is 0, 1, 2, or 3; b is 0, 1, 2, or 3; b′ is 0, 1, 2, or 3; c is 0, 1, 2, or 3; c′ is 0, 1, 2, or 3; m1 is 0, 1, or 2; m2 is 0, 1, or 2; U¹ is O, or S; U² is O, or S; T¹, T², T³ and T⁴ are independently of each other: a hydrogen, halogen, cyano, —COOR¹⁰³, —OCOR¹⁰³, —NR¹¹²COR¹⁰³, —CONR¹¹²R¹¹³, —OR^(103′), —SR^(103′), —SOR^(103′), —SO₂R^(103′), —NR¹¹²SO₂R^(103′), —NR¹¹²R¹¹³, —NO₂, C₇-C₂₅arylalkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy; a C₁-C₁₀₀alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₂-C₁₀₀alkenyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₂-C₁₀₀alkinyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₃-C₁₂cycloalkyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₆-C₂₄aryl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); a C₂-C₂₀heteroaryl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); a —CO—C₁-C₁₈alkyl group, a —CO—C₅-C₁₂cycloalkyl group, or —COO—C₁-C₁₈alkyl group; Ar¹ and Ar^(1′) are independently of each other

Ar², Ar^(2′), Ar³ and Ar^(3′) have independently of each other the meaning of Ar¹, or are independently of each other

wherein X is O, S, Se, Te, or NR⁸, X′ is O, or S, X¹, X² and X³ are independently of each other S, O, NR¹⁰⁷—, —Si(R¹¹⁷)(R^(117′))—, —Ge(R¹¹⁷)(R^(117′))—, —C(R¹⁰⁸)(R¹⁰⁹)—, —C(═O)—, —C(═CR¹¹⁰R¹¹¹)—,

X⁴ and X^(4′) are independently of each other S, O, NR¹⁰⁷—, —Si(R¹¹⁷)(R^(117′))—, —Ge(R¹¹⁷)(R^(117′))—, —C(R¹⁰⁸)(R¹⁰⁹)—, —C(═O)—, —C(═CR¹¹⁰R¹¹¹)—, R³ and R^(3′) are independently of each other hydrogen, halogen, halogenated C₁-C₂₅alkyl, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms, C₇-C₂₅arylalkyl, or C₁-C₂₅alkoxy; R⁴, R^(4′), R⁵, R^(5′), R⁶, and R^(6′) are independently of each other hydrogen, halogen, halogenated C₁-C₂₅alkyl, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms, C₇-C₂₅arylalkyl, or C₁-C₂₅alkoxy; R⁷, R^(7′), R⁹ and R^(9′) are independently of each other hydrogen, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms, or C₁-C₂₅arylalkyl; R⁸ and R^(8′) are independently of each other hydrogen, C₆-C₁₈aryl, C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl or C₁-C₁₈alkoxy, or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms, or C₇-C₂₅arylalkyl; R¹⁰ and R^(10′) are independently of each other hydrogen, halogen, NO₂, NR¹¹²R¹¹³, cyano, C₁-C₂₅alkyl, C₁-C₂₅alkyl which is substituted one or more times by E and/or interrupted one or more times by D,

 COO—C₁-C₁₈alkyl, C₄-C₁₈cycloalkyl group, C₄-C₁₈cycloalkyl group, which is substituted by G, C₂-C₁₈alkenyl, C₂-C₁₈alkynyl, C₁-C₁₈alkylthio, C₁-C₁₈alkoxy, C₁-C₁₈alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by G, or a group of formulae IVa to IVk,

wherein X⁵ is O, S, Se, Te, or NR⁵⁹, R¹¹ and R^(11′) are independently of each other C₁-C₂₅alkyl group, C₇-C₂₅arylalkyl, or a phenyl group, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₅alkoxy; R¹² and R^(12′) are independently of each other hydrogen, halogen, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one, or more oxygen, or sulphur atoms, C₁-C₂₅alkoxy, C₇-C₂₅arylalkyl, or

R¹³ is a C₁-C₈alkyl group, or a tri(C₁-C₈alkyl)silyl group; R²² to R²⁶ and R²⁹ to R⁵⁸ represent independently of each other H, halogen, cyano, NO₂, NR¹¹²R¹¹³, C₁-C₂₅alkyl, C₁-C₂₅alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by G, a C₄-C₁₈cycloalkyl group, a C₄-C₁₈cycloalkyl group, which is substituted by G, C₂-C₁₈alkenyl, C₂-C₁₈alkynyl, C₁-C₂₅alkylthio, C₁-C₂₅alkoxy, C₁-C₂₅alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, or C₇-C₂₅aralkyl, which is substituted by G, R²⁷ and R²⁸ are independently of each other hydrogen, C₁-C₂₅alkyl, halogen, cyano or C₇-C₂₅aralkyl, or R²⁷ and R²⁸ together represent alkylene or alkenylene which may be both bonded via oxygen and/or sulfur to the thienyl residue and which may both have up to 25 carbon atoms, R⁵⁹ is hydrogen, C₆-C₁₈aryl; C₆-C₁₅aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms, or C₇-C₂₅arylalkyl, R⁶⁰ is hydrogen, C₁-C₁₈haloalkyl, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms, C₁-C₁₈alkanoyl, or C₇-C₂₅arylalkyl, R¹⁰³ and R^(103′) are independently of each other hydrogen, C₁-C₁₀₀alkyl, C₁-C₂₅alkyl substituted by E and/or interrupted with D, C₂-C₂₅alkenyl, C₂-C₂₅alkenyl substituted by E and/or interrupted with D, C₇-C₂₅arylalkyl, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, C₂-C₂₀heteroaryl, or C₂-C₂₀heteroaryl which is substituted by G, R¹⁰⁴ and R^(104′) are independently of each other hydrogen, CN, C₁-C₁₈alkyl, C₆-C₁₀aryl, which may optionally be substituted by G, or C₂-C₈heteroaryl, which may optionally be substituted by G, R¹⁰⁵, R^(105′), R¹⁰⁶ and R^(106′) are independently of each other hydrogen, halogen, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₇-C₂₅arylalkyl, or C₁-C₁₈alkoxy, R¹⁰⁷ is hydrogen, C₇-C₂₅arylalkyl, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₁₈perfluoroalkyl; C₁-C₂₅alkyl, which may be interrupted by —O—, or —S—; or —COOR¹⁰³; R¹⁰³ is as defined above; R¹⁰⁸ and R¹⁰⁹ are independently of each other H, C₁-C₂₅alkyl, C₁-C₂₅alkyl which is substituted by E and/or interrupted by D, C₇-C₂₅arylalkyl, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by G, C₂-C₁₈alkenyl, C₂-C₁₈alkynyl, C₁-C₁₈alkoxy, C₁-C₁₈alkoxy which is substituted by E and/or interrupted by D, or C₇-C₂₅aralkyl, or R¹⁰⁸ and R¹⁰⁹ together form a group of formula ═CR¹¹⁰R¹¹¹, wherein R¹¹⁰ and R¹¹¹ are independently of each other H, C₁-C₈alkyl, C₁-C₁₈alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, or C₂-C₂₀heteroaryl, or C₂-C₂₀heteroaryl which is substituted by G, or R¹⁰⁸ and R¹⁰⁹ together form a five or six membered ring, which optionally can be substituted by C₁-C₁₈alkyl, C₁-C₁₈alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by G, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by G, C₂-C₁₈alkenyl, C₂-C₁₈alkynyl, C₁-C₁₈alkoxy, C₁-C₁₈alkoxy which is substituted by E and/or interrupted by D, or C₇-C₂₅aralkyl, wherein D is —CO—, —COO—, —S—, —O—, or —NR¹¹²—, E is C₁-C₈alkylthio, C₁-C₈alkoxy, CN, —NR¹¹²R¹¹³, —CONR¹¹²R¹¹³, or halogen, G is E, or C₁-C₁₈alkyl, and R¹¹² and R¹¹³ are independently of each other H; C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₁₈alkyl; or C₁-C₁₈alkyl which is interrupted by —O—, R¹¹⁴ is C₁-C₂₅alkyl, which may optionally be interrupted by one, or more oxygen, or sulphur atoms, R¹¹⁵ and R^(115′) are independently of each other hydrogen, halogen, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one, or more oxygen, or sulphur atoms, C₁-C₂₅alkoxy, C₇-C₂₅arylalkyl, or

R¹¹⁶ is a C₁-C₈alkyl group, or a tri(C₁-C₈alkyl)silyl group; R¹¹⁷ and R^(117′) are independently of each other C₁-C₂₅alkyl group, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy; R¹¹⁸, R¹¹⁹, R¹²⁰ and R¹²¹ are independently of each other hydrogen, halogen, halogenated C₁-C₂₅alkyl, cyano, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₇-C₂₅arylalkyl, or C₁-C₂₅alkoxy; R¹²² and R^(122′) are independently of each other hydrogen, C₆-C₁₈aryl, C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl or C₁-C₁₈alkoxy, or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms, or C₇-C₂₅arylalkyl; and E_(Si) is —SiR¹⁶¹R¹⁶²R¹⁶³ or —O—SiR¹⁶¹R¹⁶²R¹⁶³, wherein R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other hydrogen, C₁-C₂₅alkyl, C₃-C₁₂cycloalkyl which might optionally be substituted with C₁-C₄alkyl, C₁-C₂₅haloalkyl, C₂-C₂₅alkenyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶, C₁-C₂₅alkoxy, C₃-C₂₄(hetero)aryloxy, NR¹⁶⁷R¹⁶⁸, halogen, C₁-C₂₅acyloxy, phenyl, phenyl which is substituted 1 to 3 times by C₁-C₂₄alkyl, halogen, cyano or C₁-C₂₅alkoxy; R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other hydrogen, C₁-C₂₅alkyl, C₃-C₁₂cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₂₅haloalkyl, C₂-C₂₅alkenyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹, C₁-C₂₅alkoxy, C₃-C₂₄(hetero)aryloxy, NR¹⁶⁷R¹⁶⁸, halogen, C₁-C₂₅acyloxy, phenyl, phenyl which is substituted 1 to 3 times by C₁-C₂₄alkyl, halogen, cyano or C₁-C₂₅alkoxy; R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other hydrogen, C₁-C₂₅alkyl, C₃-C₁₂cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₂₅haloalkyl, C₂-C₂₅alkenyl, —O—Si(CH₃)₃, C₁-C₂₅alkoxy, C₃-C₂₄(hetero)aryloxy, NR¹⁶⁷R¹⁶⁸, halogen, C₁-C₂₅acyloxy, phenyl, phenyl, which is substituted 1 to 3 times by C₁-C₂₄alkyl, halogen, cyano or C₁-C₂₅alkoxy; R¹⁶⁷ and R¹⁶⁸ are independently of each other hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; or C₇-C₂₅arylalkyl; d is an integer from 1 to 50; R²¹⁴ and R²¹⁵ are independently of each other hydrogen, C₁-C₁₈alkyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, —CN or COOR²¹⁶; and R²¹⁶ is C₁-C₂₅alkyl, C₁-C₂₅haloalkyl, C₇-C₂₅arylalkyl, C₆-C₂₄aryl or C₂-C₂₀heteroaryl.
 2. The compound according to claim 1, which is a compound of formula


3. The compound according to claim 1, which is a compound of formula


4. The compound according to claim 1, wherein U¹ and U² are O.
 5. The compound according to claim 1, wherein T¹, T², T³ and T⁴ are H, a C₁-C₃₈alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, cyano, or E_(Si); and/or can optionally be interrupted by —O—, —S—, or —NR⁶⁰—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy, wherein E_(Si) is —SiR¹⁶¹R¹⁶²R¹⁶³; R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other C₁-C₈alkyl, C₅-C₆cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, —(O—SiR⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶, or phenyl; R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹, or phenyl; R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—Si(CH₃)₃, or phenyl; and d is an integer from 1 to
 10. 6. The compound according to claim 1, wherein —Ar—R¹⁰ and —Ar′—R^(10′) are independently of each other H, F, cyano, C₁-C₂₅alkyl, C₁-C₂₅alkyl substituted with one or more halogen atoms,

wherein R³ and R^(3′) are independently of each other hydrogen, F, C₁-C₂₅alkyl, or C₁-C₂₅alkoxy, R²², R²³, R²⁵, R²⁶, R²⁷, R²⁸ and R²⁹ to R³³ represent independently of each other H, F, cyano, C₁-C₂₅alkoxy, C₁-C₂₅alkyl substituted with one or more F, or C₁-C₂₅alkyl, and R²⁴ is H, F, cyano, NO₂, NR¹¹²R¹¹³, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkylthio, C₁-C₂₅alkyl substituted with one or more halogen atoms, or C₁-C₂₅alkyl; X is O, S, Se, or NR⁸, X⁵ is O, S, Se, or NR⁵⁹, R⁵⁸ is H, F, cyano, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkylthio, C₁-C₂₅alkyl substituted with one or more halogen atoms, or C₁-C₂₅alkyl; R⁸ and R⁵⁹ are hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F; or C₇-C₂₅arylalkyl, and R¹¹² and R¹¹³ are independently of each other hydrogen, C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F; or C₇-C₂₅arylalkyl.
 7. The compound according to claim 1, which is a compound of formula

wherein U₁ and U² are O, T¹ and T² are H, a C₁-C₃₈alkyl group which can optionally be interrupted by —O—, —S—, or —NR¹—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy, T³ and T⁴ are H, a C₁-C₃₈alkyl group can optionally be interrupted by —O—, —S—, or —NR⁶⁰—, wherein R⁶⁰ is C₁-C₂₅alkyl, or phenylC₁-C₄alkyl, which can be substituted one to three times with C₁-C₈alkyl and/or C₁-C₈alkoxy, and —Ar—R¹⁰ and —Ar′—R^(10′) are independently of each other H, F, cyano, C₁-C₂₅alkyl substituted with one or more fluorine atoms, C₁-C₂₅alkyl,

wherein R³ and R^(3′) are independently of each other hydrogen, F, C₁-C₂₅alkyl, or C₁-C₂₅alkoxy, R²², R²³, R²⁵, R²⁶, R²⁷, R²⁸ and R²⁹ to R³³ represent independently of each other H, F, cyano, C₁-C₂₅alkoxy, C₁-C₂₅alkyl substituted with one or more F, or C₁-C₂₅alkyl, and R²⁴ is H, F, cyano, NO₂, NR¹¹²R¹¹³, CF₃, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkyl substituted with one or more halogen atoms, or C₁-C₂₅alkyl; X is O, S, Se, or NR⁸, X⁵ is O, S, Se, or NR⁵⁹, R⁵⁸ is H, F, cyano, phenyl, C₁-C₂₅alkoxy, C₁-C₂₅alkylthio, C₁-C₂₅alkyl substituted with one or more halogen atoms, or C₁-C₂₅alkyl; R⁸ and R⁵⁹ are hydrogen, C₆-C₁₈aryl, C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl or C₁-C₁₈alkoxy, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F, or C₇-C₂₅arylalkyl, and R¹¹² and R¹¹³ are independently of each other hydrogen, C₆-C₁₈aryl, C₆-C₁₈aryl which is substituted one to three times by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms and/or is optionally substituted by one or more F, or C₇-C₂₅arylalkyl.
 8. The compound according to claim 1, which is a compound of formula


9. A polymer comprising a repeating unit of the formula —[(Ar)′—Y—(Ar′)_(z) ²]—(V), wherein z¹ and z² are independently of each other 0, or 1, Y, Ar and Ar′ are defined in claim
 1. 10. The polymer according to claim 9, comprising a repeating unit of the formula

wherein z¹ and z² are independently of each other 0, or
 1. 11. The polymer according to claim 9, comprising a repeating unit of the formula


12. The polymer according to claim 9, wherein U¹ and U² are O.
 13. The polymer according to claim 9, wherein T¹, T², T³ and T⁴ are H, a C₁-C₃₈alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, or E_(Si), and/or can optionally be interrupted by —O—, —S—, wherein E_(Si) is —SiR¹⁶¹R¹⁶²R¹⁶³; R¹⁶¹, R¹⁶² and R¹⁶³ are independently of each other C₁-C₈alkyl, C₅-C₆cycloalkyl, which might optionally be substituted with C₁-C₄alkyl; C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁴R¹⁶⁵R¹⁶⁶, —(O—SiR¹⁶⁴R¹⁶⁵)_(d)—R¹⁶⁶, or phenyl; R¹⁶⁴, R¹⁶⁵ and R¹⁶⁶ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—SiR¹⁶⁹R¹⁷⁰R¹⁷¹, —(O—SiR¹⁶⁹R¹⁷⁰)_(d)—R¹⁷¹, or phenyl; R¹⁶⁹, R¹⁷⁰ and R¹⁷¹ are independently of each other C₁-C₈alkyl, C₁-C₈haloalkyl, C₂-C₈alkenyl, —O—Si(CH₃)₃, or phenyl; d is an integer from 1 to
 10. 14. The polymer according to claim 9, wherein —Ar— and —Ar′— are independently of each other a single bond,

wherein R³ and R^(3′) are independently of each other hydrogen, F, C₁-C₂₅alkoxy, or C₁-C₂₅alkyl, R⁸ is hydrogen, or C₁-C₂₅alkyl, and R¹⁰⁴ and R^(104′) are independently of each other hydrogen, cyano, COOR¹⁰³, or a C₁-C₂₅alkyl group, wherein R¹⁰³ is a C₁-C₂₅alkyl group, which can optionally be interrupted by —O—, or —S—.
 15. The polymer according to claim 9, comprising a repeating unit of the formula *

A

* and a repeating unit *

COM¹

*, wherein A is a repeating unit of formula (V), and —COM¹- is a repeating unit, which has the meaning of Ar², or a group of formula

wherein s is 1, t is 1, u is 0 or 1, v is 0 or 1, and Ar⁴ and Ar⁵ are independently of each other a group of formula

wherein Ar¹⁴, Ar¹⁵, Ar¹⁶ and Ar¹⁷ are independently of each other a group of formula

 wherein one of X⁷ and X⁸ is N and the other is CR¹⁴, R¹⁴, R^(14′), R¹⁷ and R^(17′) are independently of each other H, F, a C₁-C₅₂alkyl group, or a C₁-C₂₅alkoxy group, R²⁰⁰ and R^(200′) are independently of each other H, or F, R²⁰¹ and R²⁰² are independently of each other H, a C₁-C₁₀₀alkyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₂-C₁₀₀alkenyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₃-C₁₀₀alkinyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₃-C₁₂cycloalkyl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si); and/or can optionally be interrupted by —O—, —S—, —NR⁶⁰—, CONR⁶⁰—, NR⁶⁰CO—, —COO—, —CO— or —OCO—, a C₆-C₂₄aryl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si), a C₂-C₂₀heteroaryl group which can optionally be substituted one or more times with C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, C₅-C₁₂cycloalkyl, nitro, cyano, vinyl, allyl, C₆-C₂₄aryl, C₂-C₂₀heteroaryl, or E_(Si), R⁶⁰ is hydrogen, C₁-C₁₈haloalkyl, C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms; C₁-C₁₈alkanoyl, or C₇-C₂₅arylalkyl, R²⁰⁶ is hydrogen, or C₁-C₂₅alkyl, or C₆-C₁₈aryl; C₆-C₁₅aryl which is substituted by C₁-C₁₈alkyl, or C₁-C₁₈alkoxy; or C₁-C₂₅alkyl, which may optionally be interrupted by one or more oxygen or sulphur atoms, and R³⁰⁴ and R^(304′) are independently of each other hydrogen, cyano, COOR³⁰⁵, or a C₁-C₂₅alkyl group, wherein R³⁰⁵ is a C₁-C₂₅alkyl group, which can optionally be interrupted by —O—, or —S—.
 16. The polymer according to claim 9, which is a polymer of the formula


17. An organic semiconductor material, layer or component, comprising a compound according to claim
 1. 18. A semiconductor device, comprising a compound according to claim
 1. 19. The semiconductor device according to claim 18, which is an organic photovoltaic device, a photodiode, or an organic field effect transistor.
 20. A process for the preparation of an organic semiconductor device, which process comprises applying a solution and/or dispersion of a compound according to claim 1 in an organic solvent to a suitable substrate and removing the solvent.
 21. A PV device, photodiode, IR absorber, or organic filed effect transistor, comprising the compound according to claim
 1. 22. A compound of formula X⁶—Ar—Y—Ar′—X^(6′)  (X), wherein Y, Ar and Ar′ are defined in claim 1, and X⁶ and X^(6′) are independently of each other halogen, ZnX¹², —SnR²⁰⁷R²⁰⁸R²⁰⁹, wherein R²⁰⁷, R²⁰⁸ and R²⁰⁹ are identical or different and are H or C₁-C₆alkyl, wherein two radicals optionally form a common ring and these radicals are optionally branched or unbranched and X¹² is a halogen atom; or —OS(O)₂CF₃, —OS(O)₂-aryl, —OS(O)₂CH₃, —B(OH)₂, —B(OY¹)₂,

 —BF₄Na, or —BF₄K, wherein Y¹ is independently in each occurrence a C₁-C₁₀alkyl group, Y² is independently in each occurrence a C₂-C₁₀ alkylene group, which can optionally be substituted by one, or more C₁-C₈alkyl groups, and Y¹³ and Y¹⁴ are independently of each other hydrogen, or a C₁-C₁₀alkyl group.
 23. The compound according to claim 22, which is a compound of formula


24. A process for producing a compound of formula

which process comprises (a) reacting a compound of formula

with a compound of formula T₁COOH (XIIa) and a compound of formula T²COOH (XIIb), or a compound of formula T₁COOH (XIIa) in a solvent in the presence of an acid and/or an acid anhydride, wherein T¹, T², T³, T⁴, U¹, U², Ar, Ar′, R¹⁰ and R^(10′) are defined in claim 1 and when compound of formula (XI) is reacted only with a compound of formula (XIIa), T² in formula (Ia) has the meaning of T¹. 